Abstract:Large-area micro surficial features can realize different functions such as reducing the flow friction and improving the hydrophobicity. However, an evident challenge is how to realize the fabrication of thousands of micro features on large area in an efficient and low-cost manner. Roller microforming process is a satisfying method in that regard. Since the dimensions of micro features are in the same level with the grain size, the so-called size effect occurs during the microforming process. To understand how the size effect influences the roll-to-plate (R2P) micro imprinting process, experimental setup was established to form micro riblet features onto the surface of copper plate. The imprinted feature height is revealed to increase with the grain size. The flow stress reduction with the increase of grain size was identified to be the major reason for the increase of forming height at the smaller grain size condition. However, an evident underestimation was revealed for the case with the grain size of 180 μm. A further study was conducted by considering the crystalline microstructures via the Voronoi algorithm. The predicted forming heights were found to agree with the experiments, suggesting the inhomogeneous deformation of individual grains could improve the formability of material in the R2P microimprinting process. The uneven nature of individual grains actually lowers the difficulty of material flow since the deformation is easier to initialize and localize at weaker grains during imprinting.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the influence of grain size effect on the height of microstructure formation in the Roll - to - Plate Micro Imprinting (R2P) process. Specifically, the researchers are concerned with how to understand and quantify the specific influence of grain size on the microstructure formation process during the large - scale, high - efficiency and low - cost manufacturing of large - area microstructure features. Through experimental and numerical simulation methods, the paper explores the height changes of micro - rib features formed on copper plates with different grain sizes during the R2P micro - forming process, and analyzes the reasons behind these changes, especially the influence of grain size effect on the material flow stress and its relationship with the polycrystalline microstructure. The study found that as the grain size increases, the height of the formed microstructure also increases, mainly because the increase in grain size leads to a decrease in the material flow stress. However, when the grain size reaches 180 μm, there is an obvious underestimation between the experimental results and the prediction results based on the traditional model. Further research shows that considering the polycrystalline microstructure (modeled by the Voronoi algorithm) can predict the formation height more accurately, because the non - uniform deformation behavior between different grains actually reduces the difficulty of material flow, making it easier for the deformation to start and concentrate at the weaker grains, thereby improving the formation efficiency of the microstructure. In summary, this paper aims to provide theoretical basis and technical support for optimizing this process by in - depth analysis of the influence of grain size effect on the R2P micro - forming process, especially in the application when the grain size is close to or larger than the size of the microstructure feature.

Investigation on the roll-to-plate microforming of riblet features with the consideration of grain size effect

An Experimental Investigation on the Fabrication of Micro/Meso Surface Features by Metallic Roll-to-Plate Imprinting Process

Grain and Geometry Size Effects on Plastic Deformation in Roll-to-plate Micro/meso-Imprinting Process

Roll-to-plate micro-imprinting of large-area surface micro features: Experiments and a local simulation method

Micro/Meso Roll-to-Plate (R2P) Imprinting Process to Fabricate Micro Channel/Riblet Features

An experimental study on a rapid micro imprinting process

Roll-to-roll Hot Embossing System with Shape Preserving Mechanism for the Large-Area Fabrication of Microstructures.

Fabrication of Seamless Roller Mould with Smooth Surface Microstructures by Rotation Lithography and Reflow Process

Grain size effect on the assembly quality of micro-scaled barrel formed by microforming

A novel macro-micro integrated incremental sheet forming process for fabricating parts with functional surface microfeatures

Study on multi-roller flow forming process of aluminum alloy cylinders with cross ribs

Investigation of hot roller embossing for microfluidic devices

Size Effect Affected Mechanical Properties and Formability in Micro Plane Strain Deformation Process of Pure Nickel

Mechanism of forming defects in roll-to-roll hot embossing of micro-pyramid arrays I: experiments

Research On Micro-Forming Process Of Aluminum And Its Alloy

Investigation of Pattern Coating on Mould Roller in Roller-Reversal Imprint Process

Experimental studies on a novel roll-to-roll powder hot embossing for large-area fabrication of micropyramid arrays on polymers

Microforming: Experimental Investigation of the Extrusion Process for Micropins and Its Numerical Simulation Using Rkem

An investigation on the friction in a micro sheet metal roll forming processes considering adhesion and ploughing

Study of Size Effects on Deformation Behavior and Formability in Micro Metal Forming of Ti Foil

Experimental investigation for roll-to-plate embossing of ordered micro-pyramid array on the silver sheet