Abstract:Cracking furnaces, operating under high temperatures and in a hydrocarbon medium, subject their tubes to complex stresses such as internal pressure, self-weight, fatigue, and thermal shock during start-up and shutdown. As a result, these furnace tubes frequently experience failures characterized by cracks and corrosion perforation. The high-temperature environment, constantly evolving structure of the tubes, and the close arrangement of the cracks within the tube box hinder detecting the cracks using conventional single-detection methods is challenging. This paper breaks through the limitations of the traditional single detection method and studies the effectiveness of the combination of ultrasonic-guided wave and low-frequency electromagnetic detection methods. The experiment was carried out by deliberately making cracks and thinning defects caused by corrosion on the cracking furnace tube of Cr35Ni45Nb after two years of service. The experimental results show that the ultrasonic guided wave detection technology can quickly detect the defects running through the whole furnace tube and effectively identify the manufacturing defects. On the other hand, low-frequency electromagnetic detection makes it possible to scan suspicious local defects and make qualitative and quantitative analyses of defect signals. The combination of ultrasonic guided wave and low-frequency electromagnetic detection can realize the rapid location and comprehensive qualitative and quantitative analysis of furnace tube defects, thus making up for the defects missed detection caused by the lack of effectiveness of single detection and the resulting safety problems. The research results have great popularization value in practical engineering applications.

Nondestructive evaluation of carburized layer depth in furnace tubes of Cr35Ni45NbMA using magnetic field distortion and magnetic attraction force measurement methods

Combining ultrasonic guided wave and low-frequency electromagnetic technology for defect detection in high-temperature Cr–Ni alloy furnace tubes

Characterization of Magnetic Field in Crack Propagation Stage and Application to Non-Destructive Evaluation

Nondestructive Testing Method for Internal Defects in Ferromagnetic Materials under Weak Bias Magnetization

Numerical Simulation of a Magnetic Corrosion Detector for Corrosion Detection of Steel Rebar in Concrete

Magnetomechanical Measurements for Nondestructive Evaluation of Failure in Steel Structural Element

Analytical Magnetic Field and Driving Force Models Based on Measured Boundary Conditions for Industrial Coriolis Mass Flowmeters

Surface Decarburization Depth Detection in Rods of 60Si2Mn Steel with Magnetic Barkhausen Noise Technique

Phase-Extraction-Based MFL Testing for Subsurface Defect in Ferromagnetic Steel Plate

Monitoring Microstructure and Properties Changes in 35CrMo Steel Components Using Magnetic Hysteresis Loop and X-Ray Diffraction Techniques

The Relationship Between Magnetism and Microstructure of Ethylene Pyrolysis Furnace Tubes after a Long-term Service

A Non-contact Detection Method for Smelting in Submerged Arc Furnace based on Magnetic Field Radiation

Magnetic and microstructural characterization of carburized HP alloy

Quantitative Nondestructive Estimation of Deep Defects in Conductive Structures

Numerical Simulation on Magnetic Flux Leakage Testing of the Steel Cable at Different Speed Title

A new Cr25Ni35Nb alloy critical failure time prediction method based on coercive force magnetic signature

Multigradient Characterization of the Strain in Low-Carbon Steel Components Based on Magnetic Barkhausen Noise Method

Magnetic Recording Method (MRM) for Nondestructive Evaluation of Ferromagnetic Materials

An Improved MFL Method Fusing Multi-Space Magnetic Field Information for The Surface Defect Inspecting

Evaluation of Depth Size Based on Layered Magnetization by Double-Sided Scanning for Internal Defects

Mechanism of Magnetic Flux Leakage Detection Method Based on the Slotted Ferromagnetic Lift-Off Layer