Abstract:When a variable magnetic field is applied to a ferromagnetic material, the change in magnetic induction occurs discontinuously as a result of the movement of magnetic domain walls. These discrete and stochastic jumps can induce, in a probe coil near the material surface, signals known as Magnetic Barkhausen Noise (MBN). MBN are sensitive to microstructural change, plastic deformation, and stress of the material. As a consequence, it can be used as a Non-Destructive Test in a large number of applications, for example to find unwanted phases, grain size control, quality control of surface treatments and degradation, detect residual stresses, etc. In this work, the on-line characterization of the transformation process of the austenite-martensite phases by deformation of stainless steel (SS) AISI 304 was studied applying the MBN technique. For this purpose, the specimens were subjected to uniaxial monotonic tensile tests up to failure. As a consequence of the plastic deformation of the SS austenitic phase, a ferromagnetic phase appears which produces MBN. The specimens were cut in two different directions considering the rolling direction (0 o and 90 o ).In order to characterize the MBN evolution with the strain, it was measured during the load increasing process applied to the specimen in uniaxial tensile tests. To characterize the transformation process, various statistical parameters were estimated which were evaluated based on the applied deformation. Finally, the temporal evolution and the Root Mean Square (RMS) function of the MBN signals were evaluated during the load increase. The MBN allowed to detect that the rolling direction of the specimens strongly influences the amount of martensite phase produced. Furthermore, it was also revealed that the MBN technique is appropriate for evaluating the initiation and evolution of the austenite-martensite phase transformation.

Multigradient Characterization of the Strain in Low-Carbon Steel Components Based on Magnetic Barkhausen Noise Method

Magnetic Barkhausen Noise Transient Analysis for Microstructure Evolution Characterization with Tensile Stress in Elastic and Plastic Status

Characterization of Magnetic Field in Crack Propagation Stage and Application to Non-Destructive Evaluation

In-Situ Magnetic Barkhausen Noise Measurements to Identify Elastic-Plastic Deformation and Failure in Different Steels

Mechanical and Magnetic Hysteresis As Indicators of the Origin and Inception of Fatigue Damage in Steel

Magnetic Barkhausen noise analysis of stress in steel

Surface Decarburization Depth Detection in Rods of 60Si2Mn Steel with Magnetic Barkhausen Noise Technique

A theoretical simulation for MBN testing: Modeling microscopic local magnetization jumps in magnetic domain movement

Tension-induced magnetic Barkhausen noise morphology transition caused by pre-introduced strain

On the Combined Effect of Elastic and Plastic Strain on Magnetic Barkhausen Noise Signals

Magnetomechanical Measurements for Nondestructive Evaluation of Failure in Steel Structural Element

Evaluation of the Magnetocrystalline Anisotropy of Typical Materials Using MBN Technology

A NEW APPROACH TO THE DETECTION OF FATIGUE DAMAGE IN RAILS USING PIEZOMAGNETIC EFFECTS

Theoretical and Experimental Investigation on the Magnetomechanical Effect of Steel Bars Subjected to Cyclic Load

A Novel Method for Characterizing the Fatigue Crack Propagation of Steel Via the Weak Magnetic Effect

Quantitative evaluation of residual stress and surface hardness in deep drawn parts based on magnetic Barkhausen noise technology

Study of martensite induced by deformation with Magnetic Barkhausen Noise Technique

Influence of Defects on Stress Detection by Magnetic Barkhausen Noise

Barkhausen Noise monitoring of microstructure and surface residual stress in maraging steel manufactured by Powder Bed Fusion and aging

Identification of Grain Oriented SiFe Steels Based on Imaging the Instantaneous Dynamics of Magnetic Barkhausen Noise Using Short-Time Fourier Transform and Deep Convolutional Neural Network

Microstructure and mechanical properties evaluation of automotive plate steel based on micromagnetic NDT technologies