Abstract:Aluminum alloys are extensively used to manufacture mechanical components. However, when exposed to alkaline environments, like lubricants, refrigerants, or detergents, they can be corroded, reducing their durability. For this reason, the aim of this study is to investigate the influence of aggressive alkaline solutions (i.e., pH and presence of chlorides) on the corrosion resistance of three aluminum alloys (AA 5083-H111, AA 6082-T6, and AA 7075-T6) with and without anodizing treatments. Open circuit potential (EOCP) and anodic polarization measurements were carried out and typical corrosion parameters such as corrosion current density (icor) and corrosion rate (CR) were determined. Morphology of the corrosion attack and samples microstructure were investigated by scanning electron microscope. Results show that corrosion behavior of the three investigated alloys is influenced by (i) the aggressiveness of the testing environments; (ii) the thickness of the anodizing treatment; (iii) the alloy chemical composition; (iv) the distribution of intermetallic phases in the aluminum matrix. Moreover, three galvanic series have been built also testing other metallic alloys commonly used in mechanical applications, i.e., carbon steel (C40), stainless-steel (AISI 304), and Cu-based alloys (Cu-Ni alloy and CW 617 N, respectively). Results clearly indicate that galvanic series play a fundamental role when it is necessary to select an alloy for a specific environment, highlighting the thermodynamic conditions for corrosion occurrence. On the other hand, kinetic measurements and microstructural studies carried out on the three aluminum alloys stress the importance of the surface treatments and relevant thickness as well as the effect of metal exposure. Future work will involve the study of other surface treatments on aluminum alloys and the evaluation of their corrosion behavior in acidic environments.

Interplay between Anodizing Parameters and Corrosion Resistance of Aluminum-Silicon Alloys

Corrosion Behavior of Aluminum Alloys in Different Alkaline Environments: Effect of Alloying Elements and Anodization Treatments

Effect of substrate microstructure on corrosion resistance of cast and forged anodised 6082 Al alloy

Anti-corrosion Performance of LY12 Al Alloy Reinforced by Anodic Oxidization and Silanization

A composite coating for corrosion protection of AM60B magnesium alloy

Anti-Corrosion Property of Atomic Layer Deposition Films for Anodized Aluminum

Improving the Corrosion Behaviour of 6061 Aluminum Alloy by Controlled Anodic Formed Oxide Layer

Critical Challenges in the Anodizing Process of Aluminium–Silicon Cast Alloys—A Review

The Effect of Sulfuric Acid Anodization on the Electrochemical Properties of Aluminum Alloy AlSi 10 Mg Prepared by Selective Laser Melting

Investigation on the Properties of Anodic Oxides Formed on Aluminium–Silicon Alloys Irradiated by Pulsed Electron Beam

Improving the Corrosion Resistance of 6061 Aluminum Alloy Using Anodization and Nickel-Cobalt based Sealing Treatment

Improving the cavitation corrosion resistance of 6061 aluminum alloy by anodizing

Effect of native air-formed oxidation on the corrosion behavior of AA 7075 aluminum alloys

Anodic Layer Growth on 1050 and 2024 Aluminium Alloys in Presence of Etidronic Acid : Changes in Morphology and Structure

Microstructure Effects on Anodizing High-Silicon Aluminium Alloy AlSi12Cu1(Fe) under Various Surface Conditions and Power Modes

Improved Corrosion Protection of Aluminum Alloys by Electrodeposited Silanes

Influence of Anodic Oxidation on the Organizational Structure and Corrosion Resistance of Oxide Film on AZ31B Magnesium Alloy

Structure, Composition and Corrosion Resistance of Mg Alloy Anodized Film

Interface strength and degradation of adhesively bonded porous aluminum oxides

Study on the Influence of Surface Treatment Process on the Corrosion Resistance of Aluminum Alloy Profile Coating