THE INFLUENCE OF PIPE STRESS STATE ON THE PITTING CORROSION RATE OF OILFIELD PIPELINES

V.I. Bolobov,I.V. Zhuikov,G.G. Popov

DOI: https://doi.org/10.17122/ngdelo-2023-4-109-120

2023-09-14

Petroleum Engineering

Abstract:An analytical review is given on the influence of the stressstrain state on the process of corrosion pitsformation in the process of internal corrosion of the field oil pipelines wall. The views of domestic and foreign researchers on the causes of the corrosion process intensification under the stresses action, as well as on the mechanisms of the stress-strain state influence on the process of pitting formation, are presented. Two main reasons for the intensification of corrosion under the stress-strain state influence are indicated: a decrease in the thermodynamic stability of metals and a deterioration in the stability of protective films formed on the stressed metal surface during corrosion. Existing concepts are considered regarding the effect of increasing the number of pitting formation zones under the action of a stress-strain state, and also put forward their own assumptions on this issue. It was found that a noticeable acceleration of the anode process is observed only when the critical level of stresses from the yield point is reached, under the conditions of field oil pipelines operation. The zones of accumulation of such a level of stresses are surface defects — stress concentrators. The process of deepening corrosion defects is accompanied by an increase in the stress concentration in the metal of their bottom part, which further accelerates the growth of their depth (the synergistic effect of mechanical and electrochemical factors on the growth rate of a surface corrosion defect). Due to the deterioration of the protective properties of passive films under stress-strain conditions, the transition from the activation stage of defect growth (when repassivation is possible) to the diffusion stage is facilitated, which leads to the formation of a larger number of steadily growing corrosion defects. At the same time, the level of accumulated stresses depends on the shape of the formed corrosion defects; with an increase in their depth, it increases, and with an increase in width, it decreases.

English Else