Enhancing the Mechanical Characteristics of Eco-Friendly Composite Materials: Taguchi and RSM Optimization
Khalissa Saada Salah Amroune Ahmed Belaadi Moussa Zaoui Ibrahim M. H. Alshaikh Djamel Ghernaout a Department of Mechanical Engineering,Faculty of Technology,University of M'sila,M'sila,Algeriab Materials and Structural Mechanics Laboratory (LMMS),University of M'sila,M'sila,Algeriac Department of Mechanical Engineering,Faculty of Technology,Université 20 Août 1955,Skikda,Algeriad Department of Civil Engineering,Faculty of Engineering,University of Science and Technology,Sana'a,Yemene Chemical Engineering Department,College of Engineering,University of Ha'il,Ha'il,Saudi Arabiaf Chemical Engineering Department,Faculty of Engineering,University of Blida,Blida,Algeria
DOI: https://doi.org/10.1080/15440478.2024.2427704
2024-11-26
Journal of Natural Fibers
Abstract:Green composites consisting of renewable or biodegradable materials are becoming more popular as environmental awareness of global waste issues grows. Among them, natural composites made of polymers have proven to work exceptionally well because of their high strength, rapid breakdown after disposal, and simplicity in processing using standard techniques. In particular, competitive mechanical performances have been demonstrated by green composites having a polymer matrix reinforced with sisal, luffa, and maize fibers at different fiber percentages of 10%, 15%, and 25%. The tensile characteristics of polymer composites reinforced with these fibers are optimized in this study by the application of Taguchi and response surface methodology. By assessing characteristics such as section size, fiber content, and fiber type simultaneously, the study attempts to produce optimal biocomposite qualities, which are then experimentally tested. Tensile tests show considerable gains: the biocomposite containing 15% corn fiber showed a 21.04% increase in tensile strength. Similarly, sisal, luffa, and corn fibers all showed notable improvements in Young's modulus, with the biocomposite showing 22.77%, 31.77%, and 20.25% increases, respectively. 随着对全球废物问题的环保意识的增强,由可再生或可生物降解材料组成的绿色复合材料越来越受欢迎. 其中,由聚合物制成的天然复合材料已被证明效果非常好,因为它们具有高强度、处理后的快速分解以及使用标准技术加工的简单性. 特别是,绿色复合材料已经证明了其具有竞争力的机械性能,该复合材料具有用剑麻、丝瓜和玉米纤维以10%、15%和25%的不同纤维百分比增强的聚合物基体. 本研究通过应用田口和响应面方法优化了用这些纤维增强的聚合物复合材料的拉伸特性. 通过同时评估截面尺寸、纤维含量和纤维类型等特征,该研究试图产生最佳的生物复合材料质量,然后进行实验测试. 拉伸试验显示了相当大的收益: 含有15%玉米纤维的生物复合材料的拉伸强度提高了21.04%. 同样,剑麻、丝瓜和玉米纤维的杨氏模量都有显著提高,生物复合材料的杨氏模量分别提高了22.77%、31.77%和20.25%.
materials science, textiles