Abstract:The core‐shell architectures, utilizing robust metal‐organic frameworks (MOFs) as core initiators and poly(1,3‐dioxolane) dimethacrylate (PDXLMA) as shell materials, are synthesized to produce an ultrathin two‐layered composite membrane without the requirement for gutter layers. The resulting defect‐free membranes show exceptional gas separation performance, achieving a CO2 permeance of up to 6,035 GPU while maintaining a CO2/N2 selectivity of >20. Increasing amounts of carbon dioxide (CO2) emissions in the atmosphere are a leading cause of climate change. Ultrathin film composite (UTFC) membranes have the potential to effectively reduce CO2 emissions from energy production and industrial processes. UTFC membranes typically require a gutter layer, to provide flat surfaces above the porous substrate for an ultrathin selective layer to be deposited. Removing the gutter layer, while maintaining compatibility with the support layer, can have substantial benefits of high gas permeation, cost‐effectiveness, and fewer manufacturing steps. However, achieving this faces significant challenges, due to limitations on the geometric design of gas pathways and incompatibility between the substrate and selective layers. Herein, zeolitic imidazolate framework‐8 (ZIF‐8) is used as an initiating core, and arms of poly(1,3‐dioxolane) dimethacrylate (PDXLMA), which possesses superior CO2/N2 selectivity, are used to create core‐shell nanoparticles. These two‐layered UTFC membranes are successfully produced from the nanoparticles via a simple drop‐spreading method. The importance of designing core‐shell structures is also investigated to achieve defect‐free two‐layered UTFC membranes and enable precision thickness control. The resulting membranes exhibit remarkable CO2 permeance of 3969 – 6035 GPU with CO2/N2 selectivity of 28.0–20.4, demonstrating their considerable performance improvement compared to the current three‐layered UTFC membranes.

Fabrication of MIL-96 nanosheets and relevant c-oriented ultrathin membrane through solvent optimization

Solvent-Less Vapor-Phase Fabrication of Membranes for Sustainable Separation Processes

Fabrication of B-Oriented MFI Zeolite Membranes by a Printing-Transfer Seed Layer Procedure.

Zeolite Imidazolate Framework Membranes on Polymeric Substrates Modified with Poly(vinyl Alcohol) and Alginate Composite Hydrogels.

Microstructure Manipulation of MFI-type Zeolite Membranes on Hollow Fibers for Ethanol–water Separation

Preparation of continuous NH2–MIL-53 membrane on ammoniated polyvinylidene fluoride hollow fiber for efficient H2 purification

Highly Durable MIL-96 Membranes via a One-step Active γ-Alumina Conversion Strategy for Gas Separation

Fabrication of ZIF-8 Membranes on Dual-Layer ZnO-PES/PES Organic Hollow Fibers by In-Situ Crystallization

Seeded growth of high-performance ZIF-8 membranes in thick wall autoclaves assisted by modulator

Twin-free, directly synthesized MFI nanosheets with improved thickness uniformity and their use in membrane fabrication

Ultrathin metal–organic framework membrane production by gel–vapour deposition

Fabrication of Functionalized MOFs Incorporated Mixed Matrix Hollow Fiber Membrane for Gas Separation

Large‐Area Fabrication of Ultrathin Metal‐Organic Framework Membranes

Solid-solvent processing of ultrathin, highly loaded mixed-matrix membrane for gas separation

Fabrication of 2D bimetallic metal-organic framework ultrathin membranes by vapor phase transformation of hydroxy double salts

Thermally Annealed High-Aspect-Ratio ZIF-8 Nanoplates-Incorporated Mixed Matrix Membranes for Improved H2/CO2 Selectivity

Preparation and gas separation performance of seeding-free aqueous synthesis ZIF-8 membrane by homologous-like ligands method

Enhancing contaminant rejection efficiency with ZIF-8 molecular sieving in sustainable mixed matrix membranes

Space-confined growth of 2D MOF sheets between GO layers at room temperature for superior PDMS membrane-based ester/water separation

Unveiling the Potential: Core‐Shell Nanoparticles Assembly of Metal‐Organic Framework@poly(1,3‐dioxolane) Methacrylate for Gutter‐Layer‐Free Ultrathin Film Composite Membranes

Functionalized MOF-Derived Nanoporous Carbon as Compatible Nanofiller to Fabricate Defect-Free PDMS-Based Mixed Matrix Pervaporation Membranes