Abstract:The average salinity of seawater is 3.5%, with a significant presence of corrosive ions, primarily Cl − and SO 4 2− . In contrast to cement engineering in terrestrial natural environments, cement-reinforced structures exposed to corrosive marine environments not only endure ion erosion but also undergo periodic desiccation due to tidal variations in seawater. The coupling of these effects results in a reduction in the mechanical properties of cemented soil, inevitably leading to the degradation of cemented foundations, posing a serious threat to their safety and normal functionality. Investigating the improvement of the mechanical properties of cemented soil in corrosive coastal environments is a crucial engineering challenge in current coastal construction projects. To address this engineering challenge, this study proposes the use of Nano-SiO 2 to enhance the mechanical characteristics of cemented soil, aiming to improve the strength and durability of cement-reinforced structures. Simulating the main corrosive ions in seawater by using different concentrations of SO 4 2− ions, the study subjected cemented soil samples to dry–wet cycles to simulate the desiccation caused by tidal changes in seawater. Unconfined compressive strength tests were conducted on cemented soil and nano-cemented soil samples under coupled conditions, revealing that the incorporation of Nano-SiO 2 increased the strength of cemented soil and slowed down the corrosion rate. With an ion concentration of 12.3 g/L, after 60 dry and wet cycles, the compressive strength of nano-cemented soil increased by 90% compared to conventional cemented soil, with a mass loss only half that of conventional cemented soil. XRD, SEM, and NMR tests on various cemented soil samples indicated that the addition of Nano-SiO 2 filled small pores, suppressed pore development, and interacted with cement hydration products, forming a gel-like structure that improved the compactness of cemented soil. This, in turn, mitigated ion corrosion and the degradation of cemented soil under dry–wet cycles.

Cavitation erosion in suspensions containing sediment and NaCl for cement paste and mortar

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack

Sedimentation-affected Engineering Performances and Microstructures of a Hybrid Portland- Sulfate Aluminate Cement Grout Cast in Long Tubes

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Degradation effect of seawater on the long-term dynamic behavior of artificially cemented sand

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Degradation characteristics of Portland cement mortar incorporating supplementary cementitious materials under multi-ions attacks and drying-wetting cycles

Chloride Ingress Profiles and Binding Capacity of Mortar in Cyclic Drying-Wetting Salt Fog Environments

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Effect of modified supplementary cementitious material on performance of mortar and concrete in marine environment

A Substitute for Portland Cement: Experiments on Ecofriendly Reinforcement of Large-Scale Calcareous Sand by Microbial-Induced Carbonate Precipitation Spraying Method

Degradation progress of Portland cement mortar under the coupled effects of multiple corrosive ions and drying-wetting cycles

Experimental study on the mesoscale causes of the effect of sediment size and concentration on material cavitation erosion in sandy water

Erosion of Aerial Lime and Sticky Rice Mortars by Cyclic Wetting–drying and Dilute Sulfate Acid Actions

Effects of Seawater, NaCl, and [math] Solution Mixing on Hydration Process of Cement Paste

Research on Synergistic Erosion by Cavitation and Sediment: A Review

Improved mechanical response of Nano-SiO2 powder cemented soil under the coupling effect of dry and wet cycles and seawater corrosion

Erosion characteristics and failure mechanism of reservoir rocks under the synergistic effect of ultrasonic cavitation and micro-abrasives

Investigation on chloride resistance of high-volume slag low-carbon cement-based materials with crystalline admixture under seawater

Deteriorated characteristics, elemental zonation, and phase changes in the surface of cemented soil exposed to marine environment

Research on the Permeability and Pore Structure Distribution Characteristics of High-Performance Mortar for Surface Treatment of Bridge Piers and Columns