Abstract:In this paper, the damage initiation/propagation mechanisms and failure modes of open-hole carbon fiber-reinforced thermoplastic composites and thermosetting composites with tension, compression, and bearing loads are investigated, respectively, by experiments and finite element simulations. The experimental evaluations are performed on the specimens using the Combined Loading Compression (CLC) test method, the tensile test method, and the single-shear test method. The differences in macroscopic damage initiation, evolution mode, and damage characteristics between thermoplastic composite materials and thermosetting composite material open-hole structures are obtained and analyzed under compressive load. Based on scanning electron microscope SEM images, a comparative analysis is conducted on the micro-failure modes of fibers, matrices, and fiber/matrix interfaces in the open-hole structures of thermoplastic and thermosetting composites under compressive load. The differences between thermoplastic and thermosetting composites were analyzed from the micro-failure mechanism. Finally, based on continuum damage mechanics (CDM), a damage model is also developed for predicting the initiation and propagation of damage in thermoplastic composites. The model, which can capture fiber breakage and matrix crack, as well as the nonlinear response, is used to conduct virtual compression tests, tensile test, and single-shear test, respectively. Numerical simulation results are compared with the extracted experimental results. The displacement-load curve and failure modes match the experimental result, which indicates that the finite element model has good reliability.

Numerical and Experimental Study of Crack Propagation in the Tensile Composite Plate with the Open Hole

Failure Mechanism of Tensile CFRP Composite Plates with Variable Hole Diameter

Numerical simulation and experiment validation of variable stiffness composite laminates with open holes under unidirectional tension

Dynamic Crack Growth in a Fiber-Reinforced Composite Plate

THE STUDY ON TESTS AND NUMERICAL SIMULATION OF CRACK PROPAGATION PROBLEM IN DELAMINATION FAILURE OF COMPOSITE LAMINATED PLATE

Analysis of the Effect of an Open Hole on the Buckling of a Compressed Composite Plate

Experimental and Numerical Study on Fiber Reinforced Composite Plate with Cavity under Impact Loading

Experimental-Numerical Failure Analysis of Thin-Walled Composite Columns Using Advanced Damage Models

Progressive Failure Analysis of Thin-Walled Composite Structures Verified Experimentally

Experimental Data on Fracture of Open-Hole Composite Laminates Subjected to Tension Loading

A Comparative Study on the Mechanical Properties of Open-Hole Carbon Fiber-Reinforced Thermoplastic and Thermosetting Composite Materials

Numerical Study on Crack Propagation in Linear Elastic Multiphase Composite Materials Using Phase Field Method

Progressive Failure Analysis of an Open-Hole Composite Laminate by Using the S-Version Finite-Element Method

Stability and Failure of Thin-Walled Composite Plate Elements with Asymmetric Configurations

Failure analysis and experimental study on bolted composite joints based on continuum damage mechanics

Experimental and numerical investigation of damage evolution in carbon fiber reinforced polymer stiffened panel in post-buckling regime

Experiments and Numerical Analysis of Damage and Fracture Process on Plates with a Round Hole

Ductile Failure of Flat Plates Containing Two Through-Wall Cracks: Experimental Investigation and Numerical Modeling

Experimental and Numerical Investigations of Composite Plates Under Impact Load

Experimental Study on Carbon Fiber/epoxy Laminates under Dynamic Tensile and Their Damage Analysis

Transverse Cracking of Orthotropic Composite Laminates: a Fracture Mechanics Approach