Abstract:Objectives: Lithium disilicate (LDS) based glass ceramics are indispensable materials in the field of prosthetic dentistry due to their strength and excellent esthetics. Recently, novel fully crystallized LDS for the milling process have been introduced to the market, requiring only chairside polishing before delivery. Since limited data is available about subjecting this material to glazing, this study aimed to evaluate the wear properties, fracture resistance, and optical properties of the newly introduced fully crystallized LDS after glazing. Methods: Lithium disilicate glass-ceramics (fully crystallized (LiSiCAD) and partially crystallized types (EmaxCAD), of shade A3, were used in the present study. The fully crystallized specimens were subjected to a glazing firing cycle in a furnace (LiSiCAD-G) and compared to a polished fully crystallized counterpart (LiSiCAD-P, negative control) and a glazed partially crystallized LDS (EmaxCAD, positive control). Rectangular-shaped ceramic specimens (n = 10, 12 × 6.5 × 1.5 mm) and enamel antagonists were used to test the wear resistance in a specially designed wear machine built at the Department of Oral Technology, University of Bonn, Germany. The volumetric enamel loss of antagonists was measured by means of overlapping virtual 3D models derived from micro-CT scans for the teeth before and after the wear test. The weight loss of ceramic specimens in milligrams was measured after 100,000 and 200,000 wear cycles. A spectrophotometer was used to calculate the CIELAB color parameters of the ceramic specimens against black and white backgrounds to measure the translucency. Fracture resistance was also assessed after thermodynamic fatigue using a universal testing machine until fracture at a 1 mm/min crosshead speed. Statistical analysis was performed using one-way ANOVA and the significance level was set at α = 0.05. Results: EmaxCAD and LisiCAD-G groups showed significantly higher mean ceramic weight loss after 100,000 cycles (2 ± 0.3 mg and 1.93 ± 0.2 mg, respectively) than LisiCAD-P group (0.78 ± 0.19 mg). Glazed LiSiCAD specimens demonstrated significantly higher ΔE values from shade A3 compared to polished LiSiCAD. There was no significant difference in ΔE between LiSiCAD-G and EmaxCAD. For fracture resistance, no significant difference was observed between LiSiCAD-G and LiSiCAD-P before or after aging. Conclusions: The glazed fully crystallized LDS was superior to the partially crystallized one with regard to wear resistance but showed more color changes than the polished fully crystallized one. Furthermore, polishing of fully crystallized LDS could still be considered a better option than glazing when aesthetics is a primary prerequisite.

Does glaze firing affect the strength of advanced lithium disilicate after simulated defects?

Effect of glazing technique and firing on surface roughness and flexural strength of an advanced lithium disilicate

Impact of glazing on wear, fracture load, and optical properties of a new fully crystallized lithium disilicate ceramic material

Long-term effect of firing protocols on surface roughness and flexural strength of lithium disilicate glass-ceramic

Strength-limiting damage and its mitigation in CAD-CAM zirconia-reinforced lithium-silicate ceramics machined in a fully crystallized state

Glass science behind lithium silicate glass-ceramics

Strength-limiting damage in lithium silicate glass-ceramics associated with CAD-CAM

Crystal Phase Formation and Mechanical Properties of Lithium Disilicate Glass-Ceramics for Dental Restoration

Effect of different design and surface treatment on the load-to-failure of ceramic repaired with composite

Effect of Glazing Protocol on the Surface Roughness and Optical Properties of Lithia-Based Glass-Ceramics

Effect of different surface treatments on optical, colorimetric, and surface characteristics of a lithium disilicate glass-ceramic

Effect of "fast"-crystallization and simultaneous glazing on physicochemical properties of lithium-disilicate CAD/CAM ceramic

Adhesion to lithium disilicate glass-ceramics after aging: Resin viscosity and ceramic surface treatment effects

Enhancing Shear Bond Strength in Lithium Silicate Glass Ceramics: Surface Treatment Optimization for Reseating Protocols

Influence of Different Surface Finishing Protocols on the Wear Behavior of Lithium Disilicate Glass-Ceramics

Improved performances of lithium disilicate glass-ceramics by seed induced crystallization

Influence of CAD/CAM milling, sintering and surface treatments on the fatigue behavior of lithium disilicate glass ceramic

Effect of repeated firing on the topographical, optical, and mechanical properties of fully crystallized lithium silicate-based ceramics

Impact of Thermal Shock Cycles on Mechanical Properties and Microstructure of Lithium Disilicate Dental Glass-Ceramic

Extended glaze firings for porcelain-veneered zirconia: Effects on the mechanical and optical behavior

Effect of glazing and thermocycling on the fracture toughness and hardness of a New fully crystallized aluminosilicate CAD/CAM ceramic material