Abstract:Objectives: Lithium disilicate (LDS) based glass ceramics are indispensable materials in the field of prosthetic dentistry due to their strength and excellent esthetics. Recently, novel fully crystallized LDS for the milling process have been introduced to the market, requiring only chairside polishing before delivery. Since limited data is available about subjecting this material to glazing, this study aimed to evaluate the wear properties, fracture resistance, and optical properties of the newly introduced fully crystallized LDS after glazing. Methods: Lithium disilicate glass-ceramics (fully crystallized (LiSiCAD) and partially crystallized types (EmaxCAD), of shade A3, were used in the present study. The fully crystallized specimens were subjected to a glazing firing cycle in a furnace (LiSiCAD-G) and compared to a polished fully crystallized counterpart (LiSiCAD-P, negative control) and a glazed partially crystallized LDS (EmaxCAD, positive control). Rectangular-shaped ceramic specimens (n = 10, 12 × 6.5 × 1.5 mm) and enamel antagonists were used to test the wear resistance in a specially designed wear machine built at the Department of Oral Technology, University of Bonn, Germany. The volumetric enamel loss of antagonists was measured by means of overlapping virtual 3D models derived from micro-CT scans for the teeth before and after the wear test. The weight loss of ceramic specimens in milligrams was measured after 100,000 and 200,000 wear cycles. A spectrophotometer was used to calculate the CIELAB color parameters of the ceramic specimens against black and white backgrounds to measure the translucency. Fracture resistance was also assessed after thermodynamic fatigue using a universal testing machine until fracture at a 1 mm/min crosshead speed. Statistical analysis was performed using one-way ANOVA and the significance level was set at α = 0.05. Results: EmaxCAD and LisiCAD-G groups showed significantly higher mean ceramic weight loss after 100,000 cycles (2 ± 0.3 mg and 1.93 ± 0.2 mg, respectively) than LisiCAD-P group (0.78 ± 0.19 mg). Glazed LiSiCAD specimens demonstrated significantly higher ΔE values from shade A3 compared to polished LiSiCAD. There was no significant difference in ΔE between LiSiCAD-G and EmaxCAD. For fracture resistance, no significant difference was observed between LiSiCAD-G and LiSiCAD-P before or after aging. Conclusions: The glazed fully crystallized LDS was superior to the partially crystallized one with regard to wear resistance but showed more color changes than the polished fully crystallized one. Furthermore, polishing of fully crystallized LDS could still be considered a better option than glazing when aesthetics is a primary prerequisite.

Effect of glazing technique and firing on surface roughness and flexural strength of an advanced lithium disilicate

Effect of Glazing Protocol on the Surface Roughness and Optical Properties of Lithia-Based Glass-Ceramics

Does glaze firing affect the strength of advanced lithium disilicate after simulated defects?

Long-term effect of firing protocols on surface roughness and flexural strength of lithium disilicate glass-ceramic

Impact of glazing on wear, fracture load, and optical properties of a new fully crystallized lithium disilicate ceramic material

Optical properties of advanced lithium disilicate

Effect of repeated firing on the topographical, optical, and mechanical properties of fully crystallized lithium silicate-based ceramics

Effect of multiple firings on optical and mechanical properties of Virgilite-containing lithium disilicate glass-ceramic of varying thickness

The Effect of Multiple Firing on the Color, Translucency, and Flexural Strength of Newly Introduced Lithium Disilicate Ceramics

Effect of Two Polishing Systems on Surface Roughness, Topography, and Flexural Strength of a Monolithic Lithium Disilicate Ceramic

Effect of different surface treatments on optical, colorimetric, and surface characteristics of a lithium disilicate glass-ceramic

Optimization of heat treatment program and effect of heat treatment on microstructure and flexural strength of micro-nano-Li2Si2O5 whisker-reinforced glass-ceramics

Translucency and Strength of Lithium Disilicate for Computer-Aided Design and Manufacturing at Different Thermal Temperatures and Thicknesses: An In Vitro Study

Optimization of heat treatment program and effect of heat treatment on microstructure and flexural strength of micro-nano-Li<sub>2</sub>Si<sub>2</sub>O<sub>5</sub> whisker-reinforced glass-ceramics

Crystal Phase Formation and Mechanical Properties of Lithium Disilicate Glass-Ceramics for Dental Restoration

Effects of Surface Roughness on the Time-Dependent Wear Performance of Lithium Disilicate Glass Ceramic for Dental Applications.

Effect of "fast"-crystallization and simultaneous glazing on physicochemical properties of lithium-disilicate CAD/CAM ceramic

Improved performances of lithium disilicate glass-ceramics by seed induced crystallization

Controlling the microstructure and properties of lithium disilicate glass-ceramics by adjusting the content of MgO

Effects of MO (M = Mg, Ca, Ba) on Crystallization and Flexural Strength of Semi-Transparent Lithium Disilicate Glass-Ceramics

Characteristic fatigue strength and reliability of dental glass-ceramics: Effect of distinct surface treatments - Hydrofluoric acid etching and silane treatment vs one-step self-etching ceramic primer