Abstract:Objectives: Lithium disilicate (LDS) based glass ceramics are indispensable materials in the field of prosthetic dentistry due to their strength and excellent esthetics. Recently, novel fully crystallized LDS for the milling process have been introduced to the market, requiring only chairside polishing before delivery. Since limited data is available about subjecting this material to glazing, this study aimed to evaluate the wear properties, fracture resistance, and optical properties of the newly introduced fully crystallized LDS after glazing. Methods: Lithium disilicate glass-ceramics (fully crystallized (LiSiCAD) and partially crystallized types (EmaxCAD), of shade A3, were used in the present study. The fully crystallized specimens were subjected to a glazing firing cycle in a furnace (LiSiCAD-G) and compared to a polished fully crystallized counterpart (LiSiCAD-P, negative control) and a glazed partially crystallized LDS (EmaxCAD, positive control). Rectangular-shaped ceramic specimens (n = 10, 12 × 6.5 × 1.5 mm) and enamel antagonists were used to test the wear resistance in a specially designed wear machine built at the Department of Oral Technology, University of Bonn, Germany. The volumetric enamel loss of antagonists was measured by means of overlapping virtual 3D models derived from micro-CT scans for the teeth before and after the wear test. The weight loss of ceramic specimens in milligrams was measured after 100,000 and 200,000 wear cycles. A spectrophotometer was used to calculate the CIELAB color parameters of the ceramic specimens against black and white backgrounds to measure the translucency. Fracture resistance was also assessed after thermodynamic fatigue using a universal testing machine until fracture at a 1 mm/min crosshead speed. Statistical analysis was performed using one-way ANOVA and the significance level was set at α = 0.05. Results: EmaxCAD and LisiCAD-G groups showed significantly higher mean ceramic weight loss after 100,000 cycles (2 ± 0.3 mg and 1.93 ± 0.2 mg, respectively) than LisiCAD-P group (0.78 ± 0.19 mg). Glazed LiSiCAD specimens demonstrated significantly higher ΔE values from shade A3 compared to polished LiSiCAD. There was no significant difference in ΔE between LiSiCAD-G and EmaxCAD. For fracture resistance, no significant difference was observed between LiSiCAD-G and LiSiCAD-P before or after aging. Conclusions: The glazed fully crystallized LDS was superior to the partially crystallized one with regard to wear resistance but showed more color changes than the polished fully crystallized one. Furthermore, polishing of fully crystallized LDS could still be considered a better option than glazing when aesthetics is a primary prerequisite.

Influence of CAD/CAM milling, sintering and surface treatments on the fatigue behavior of lithium disilicate glass ceramic

Strength-limiting damage in lithium silicate glass-ceramics associated with CAD-CAM

Strength-limiting damage and its mitigation in CAD-CAM zirconia-reinforced lithium-silicate ceramics machined in a fully crystallized state

Effects of Surface Roughness on the Time-Dependent Wear Performance of Lithium Disilicate Glass Ceramic for Dental Applications.

Effect of repeated firing on the topographical, optical, and mechanical properties of fully crystallized lithium silicate-based ceramics

Influence of Different Surface Finishing Protocols on the Wear Behavior of Lithium Disilicate Glass-Ceramics

Brittle–Ductile Threshold in Lithium Disilicate under Sharp Sliding Contact

Sliding contact wear and subsurface damage of CAD/CAM materials against zirconia

Characteristic fatigue strength and reliability of dental glass-ceramics: Effect of distinct surface treatments - Hydrofluoric acid etching and silane treatment vs one-step self-etching ceramic primer

Response of pre-crystallized CAD/CAM zirconia-reinforced lithium silicate glass ceramic to cyclic nanoindentation

Long-term effect of firing protocols on surface roughness and flexural strength of lithium disilicate glass-ceramic

Lifetime-limiting strength degradation from contact fatigue in dental ceramics

Polishing the bonding surface, before or after crystallization, does not alter the fatigue behavior of bonded CAD-CAM lithium disilicate

Soft machining-induced surface and edge chipping damage in pre-crystalized lithium silicate glass ceramics

Effects of different surface treatments on the cyclic fatigue strength of one-piece CAD/CAM zirconia implants.

Determination of the mechanical behavior of lithium disilicate glass ceramics by nanoindentation & scanning probe microscopy

Impact of glazing on wear, fracture load, and optical properties of a new fully crystallized lithium disilicate ceramic material

Effect of Core Ceramic Grinding on Fracture Behaviour of Bilayered Lithium Disilicate Glass–ceramic under Two Loading Schemes

Effects of Crystal Refining on Wear Behaviors and Mechanical Properties of Lithium Disilicate Glass-Ceramics.

Effect of different CAD/CAM cutting depths on the post-fatigue load-bearing capacity of novel multilayer zirconia restorations

Influence of Cyclic Loading on the Fracture Toughness and Load Bearing Capacities of All-Ceramic Crowns