Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

F atigue behaviors of a nickel-based superalloy after hot-corrosion: Experiments and peridynamic simulations

Fatigue Behaviors of a Nickel-Based Superalloy after Hot-Corrosion: Experiments and Peridynamic Simulations

Mechanical-chemical-coupled Peridynamic Model for the Corrosion Fatigue Behavior of a Nickel-Based Alloy

Investigation of fatigue mesoscopic mechanical properties of a nickel-based superalloy by instrumented microindentation measurements

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

A Study of Fatigue Mesoscopic Elasto-Plastic Properties of a Nickel-Base Superalloy by Instrumented Microindentation Measurements

Influence of hot corrosion on thermal fatigue behavior of Ni-based single crystal superalloy: invisible and accelerated crack

The mechanism of thermal corrosion fatigue (TCF) on nickel-based single crystal superalloy and the corresponding structure shape effect

Review on Thermo-Mechanical Fatigue Behavior of Nickel-Base Superalloys

High-temperature hot-corrosion effects on the creep–fatigue behavior of a directionally solidified nickel-based superalloy: Mechanism and lifetime prediction

Fatigue Behavior and Life Prediction Model of A Nickel-Base Superalloy under Different Strain Conditions

A Model for the Determination of Residual Fatigue Life of A Nickel-Based Superalloy

Fatigue and Fracture Behaviors of Nickel-Based Forging Gh4169 Superalloy and Optimization of Model Parameters

High Temperature Fatigue and Creep-Fatigue Behaviors in a Ni-based Superalloy: Damage Mechanisms and Life Assessment

Effect Of Heat Treatment Process On Microstructure And Fatigue Behavior Of A Nickel-Base Superalloy

Corrosion fatigue testing: the combined effect of stress and high temperature corrosion

Environmentally Assisted Fatigue Evaluation Model of Alloy 690 Steam Generator Tube in High-Temperature Water

In-phase Thermomechanical Fatigue Lifetime Prediction of Nickel-Based Single Crystal Superalloys from Smooth Specimens to Notched Specimens Based on Coupling Damage on Critical Plane

Fatigue Life Prediction of Film-cooling Hole Specimens with Initial Damage

Life Assessment of Multiaxial Thermomechanical Fatigue of a Nickel-Based Superalloy Inconel 718

Evolution of fatigue mechanical properties and micro defects in nickel-based single crystal superalloys: A molecular dynamics research