Abstract:A medium-carbon Si-Mn-Ni-Cr-Mo alloyed (300M) steel was austempered for various short periods at its martensite-starting temperature of 285°C to seek improved sliding wear resistance as compared to the traditional martensitic and bainitic steels. Reciprocating sliding wear tests were performed against a WC/Co ball counterpart at a constant load of 50 N. The samples were characterised using field emission SEM, XRD and hardness testing. The associated wear mechanisms were analysed using SEM and cross-sectional TEM. The results revealed that a short austempering time of 6 minutes produced refined arrays of initial nano-bainitic ferrite laths and inter-lath filmy austenite and the majority martensite and retained austenite, while the majority of the microstructure remained martensitic with retained austenite. The hardness was unchanged to that of the as-quenched martensite of 6.4 GPa. Simultaneously the wear coefficient decreased by 41% from 2.67 to 1.58 × 10-15 m3N-1m-1, which is also superior to both the tempered martensite at 1.65 × 10-15 m3N-1m-1 and the lower bainite at 1.87 × 10-15 m3N-1m-1. Increasing the austempering time to 20 and 60 minutes resulted in wear coefficients of 1.38 and 2.18 × 10-15 m3N-1m-1, respectively. The improved wear resistance has been explained by the wear induced microstructure evolution, especially the carbon partitioning induced stabilisation of retained austenite. The high-stress sliding wear was found to be dominated by severe shear deformation, which resulted in a nano-laminate structured top layer. Delamination wear was found to take place within the embrittled nano-laminates.

Sliding wear behaviour of austempered ductile iron, boron steel and AISI 1045 steel of similar hardness: effect of microstructure, yield strength, and strain hardening

Tribological behavior of austempered ductile iron (ADI) obtained at different austempering temperatures

Wear Behavior Of Steel 1080 With Different Microstructures During Dry Sliding

Tribological behaviour and wear mechanism of ADI with different hardness values

Microstructure, Mechanical, and Wear Properties of Al-Alloyed Austempered Ductile Irons

Sliding wear of medium-carbon bainitic/martensitic/austenitic steel treated by short-term low-temperature austempering

Frictional Hardening and Softening of Steel 52100 During Dry Sliding

Effect of Ageing Temperature on the Hardness, Microstructural and Dry Sliding Wear Performance of the Functionally Graded A356 Alloy

New insight into the dry rolling-sliding wear mechanism of carbide-free bainitic and pearlitic steel

Investigating the wear resistance of AISI 410/AISI 2205 hybrid weld cladding on annealed EN 8 medium carbon steel

Tribological behavior of heat treated AISI 6150 steel

Sliding wear resistance and worn surface microstructure of nanostructured bainitic steel

Statistical significance of the sliding wear test parameters under lubricated conditions on borided AISI 316 L-SS samples

Running-in Period During Sliding Wear of Austenitic Steels

Microstructure, Wear Behavior and Surface Hardening of Austempered Ductile Iron

Sliding Wear Behavior of Laser Surface Hardened Austempered Ductile Iron

Sliding friction and wear behaviour of ion nitrided and TiN coated AISI 4140 steel

Influence of Microstructural Characteristics on the Mechanical and Wear Behavior of Wire Arc Additive Manufactured and Cast Eutectic Al-Si Alloy

Effect of Surface Melting and Chromium Surface Alloying on Wear Behavior of Ductile Iron

Dependence of Fretting Wear Resistance on Microstructural Features of Alloyed Steels

Tribological Properties of AISI 52100 Bearing Steel under Different Sliding Distance and Normal Force Conditions