SyamSai Ravuri,Pawel S Wrobel,Sandeep Gorantla,Calliope Bazioti,Martin F Sunding,Krzysztof Lis,Roman Jedrzejewski,Sabrina Sartori,Spyros Diplas,Anette E Gunnæs,Alicja Bachmatiuk,Syamsai Ravuri,Anette Gunnaes
Abstract:Synthesis of Mo2C bare MXenes, without surface terminations groups, via chemical vapor deposition (CVD) on metal foils is scientifically a very intriguing crystal growth process, and there are still challenges and limited fundamental understanding to overcome to obtain high yield and wide crystal size lateral growth. Achieving large area coverage via direct growth is scientifically vital to utilize the full potential of their unique properties in different applications. In this study, we sought to expand the boundaries of the current CVD growth approach for Mo2C MXenes and gain insights into the possibilities and limitations of large area growth, with a particular focus on controlling Mo concentration. We report a facile modification of their typical CVD growth protocol and show its influence on the Mo2C synthesis, with growth times spanning up to 3 hours. Specifically, prior to initiating the CVD growth process, we introduced a holding step in temperature at 1095 °C. This proved to be beneficial in increasing the Mo concentration on the liquid Cu growth surface. We achieved an average Mo2C crystals coverage of approximately 50% of the growth substrate area, increased tendency of coalescence and merging of individual flakes, and lateral flake sizes up to 170 μm wide. To gain deeper understanding into their CVD growth behavior, we conducted a systematic investigation of the effect of several factors, including (i) a holding step time on Mo diffusion rate through molten Cu, (ii) the Cu foil thickness over the Mo foil, and (iii) the CVD growth time. Phase, chemical and microstructural characterization by XRD, XPS, SEM and S/TEM revealed that the grown crystals are single phase α-Mo2C. Furthermore, insights gained from this study sheds light on crucial factors and inherent limitations that are essential to consider and may help guide future research progress in CVD growth of bare MXenes.
materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology
What problem does this paper attempt to address?
The problem that this paper attempts to solve is the synthesis of α - Mo₂C (molybdenum carbide) crystals with high yield and large - area growth through chemical vapor deposition (CVD) technology. Specifically, the researchers hope to explore the key factors affecting the growth of α - Mo₂C crystals, especially the methods of controlling the molybdenum (Mo) concentration, by improving the existing CVD growth methods, so as to achieve crystal growth with higher coverage and larger lateral size.
### Research Background and Problems
1. **Unique Properties of MXenes Materials**
- MXenes are a class of two - dimensional transition metal carbides or nitrides, which have excellent mechanical, electrical, thermal properties and chemical stability, and thus have broad application potential in fields such as energy storage, sensors, catalysts and electromagnetic interference shielding.
2. **Limitations of Traditional Synthesis Methods**
- The traditional MXenes synthesis method is mainly to extract from 3D MAX - phase materials through wet - chemical etching, but this method will cause the MXenes surface to be terminated by functional groups (such as O, OH, F), thus affecting its performance.
- In order to overcome this limitation, researchers began to explore bottom - up synthesis methods, especially CVD and solid - state reaction synthesis, to directly grow MXenes without surface functional groups.
3. **Challenges in CVD Synthesis of Mo₂C**
- Although the CVD synthesis of Mo₂C has been successfully achieved, there are still some challenges in current research, such as the growth of high - yield, large - area coverage and large - size crystals has not been achieved yet.
- Existing research mainly focuses on parameters such as gas flow rate and copper foil thickness, but less research has been done on other factors that may affect Mo concentration.
### Research Objectives
- **Increase the Growth Coverage and Crystal Size of Mo₂C**: By introducing a holding step, keep the temperature at 1095 °C for a period of time before CVD growth to increase the Mo concentration on the Cu liquid surface.
- **Optimize Growth Conditions**: Study the effects of different holding times, Cu foil thicknesses and CVD growth times on the growth of Mo₂C, and find the optimal growth conditions.
- **Understand the Growth Mechanism**: Through systematically studying the effects of different factors on the CVD growth behavior of Mo₂C, reveal its growth mechanism and internal limitations, and provide guidance for future CVD growth research.
### Main Findings
- **Influence of the Holding Step**
- The introduction of the holding step significantly increases the Mo concentration on the Cu liquid surface and promotes the growth of Mo₂C.
- The optimal holding time is 2 hours. At this time, the coverage rate of Mo₂C reaches about 50%, and the lateral coalescence phenomenon of crystals is observed, and the maximum lateral size can reach 170 µm.
- **Optimization of Growth Conditions**
- The optimal growth conditions are: the holding step time is 2 hours, the CVD growth time is 3 hours, and two layers of 25 µm - thick Cu foils are used to wrap a 100 µm - thick Mo foil as the growth substrate.
- Under these conditions, the coverage rate of Mo₂C reaches at least 50%, and the lateral size of the crystals is relatively large.
### Conclusion
By introducing the holding step and optimizing the growth conditions, the researchers have successfully increased the growth coverage and crystal size of Mo₂C, providing an important reference for the large - area preparation of MXenes materials in the future. This research not only helps to understand the CVD growth mechanism of Mo₂C, but also provides new ideas for the synthesis of other two - dimensional materials.