A high-strength heat-resistant Al−5.7Ni eutectic alloy with spherical Al3Ni nano-particles by selective laser melting

Junwang Deng,Chao Chen,Xiaochun Liu,Yunping Li,Kechao Zhou,Shengmin Guo
DOI: https://doi.org/10.1016/j.scriptamat.2021.114034
IF: 6.302
2021-10-01
Scripta Materialia
Abstract:<p>Traditional high-strength wrought aluminum alloys are sensitive to cracks in additive manufacturing (AM) while the eutectic aluminum alloys can be reliably printed. To explore a high-strength heat-resistant aluminum alloys by AM, in this paper, we proposed to retard the solidification range by using an Al−5.7Ni alloy, thus alleviate crack formation tendency. The AM parts of this alloy was featured by uniformly distributed spherical Al<sub>3</sub>Ni nano-particles with an average size of ~33 nm, showing a novel coherent crystallographic relationship with the matrix, &lt;110&gt;<sub>Al</sub>//&lt;113&gt;<sub>Al3Ni</sub> and {111}<sub>Al</sub>//{211}<sub>Al3Ni</sub>. Excellent mechanical property was achieved in this crack-free alloy with tensile strength of 410 MPa at room temperature and 140 MPa at 300°C, mainly attributed to the dispersion strengthening from the Al<sub>3</sub>Ni nano-particles with superior thermal stability.</p>
materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem that this paper attempts to solve is: how to prepare high - strength, heat - resistant and crack - free Al - Ni eutectic alloy (Al - 5.7Ni) through Selective Laser Melting (SLM) technology. Traditional high - strength aluminum alloys are prone to cracking during the SLM process, which limits their application in additive manufacturing. The Al - Ni eutectic alloy is considered a potential solution because of its small solidification range and low cracking tendency. Specifically, the author attempts to solve the cracking problem through the following methods by using the Al - 5.7Ni alloy: 1. **Reduce the solidification range**: By selecting the Al - 5.7Ni alloy, the solidification range is reduced, thereby reducing the tendency of crack formation. 2. **Optimize SLM process parameters**: By adjusting parameters such as laser power and scanning speed, crack - free SLM parts are prepared. 3. **Microstructure control**: Utilize the high cooling rate during the SLM process to form fine spherical Al₃Ni nanoparticles. These particles form a new coherent crystallographic relationship with the matrix, thereby improving the mechanical properties of the material. The experimental results show that through the above methods, crack - free Al - 5.7Ni alloy parts are successfully prepared. Its tensile strength at room temperature reaches 410 MPa, and the tensile strength at 300 °C still remains at 140 MPa, showing excellent mechanical properties and thermal stability. These properties are mainly attributed to the dispersion strengthening effect of Al₃Ni nanoparticles and the strengthening effect of the supersaturated solid solution in the matrix.