Abstract:We analysed the variation and effect of oxygen vacancies on the structural, dielectric and magnetic properties in case of Mn (4%) and Co (1, 2 and 4%) co-doped ZnO nanoparticles (NPs), synthesized by chemical precipitation route and annealed at 750 °C for 2 h. From the XRD, the calculated average crystallite size increased from15.30 ± 0.73 nm to 16.71 ± 012 nm, when Co content is increased from 1 to 4%. Enhancement of dopants (Mn, Co) introduced more and more oxygen vacancies to ZnO lattice confirmed from EDX and XPS. The high-temperature annealing leads to reduction of the dielectric properties due to enhancement in grain growth (large grain volume and lesser number of grain boundaries) with the incorporation of Co and Mn ions into the ZnO lattice. The electrical conductivity of the Mn doped and (Mn, Co) co-doped ZnO samples were enhanced due to increase in the volume of conducting grains and charge density (liberation of trapped charge carriers in oxygen vacancies and free charge carriers at higher frequencies). The Mn-doped and (Mn, Co) co-doped ZnO NPs show ferromagnetic (FM) behaviour. The saturation and remnant magnetizations (Ms and Mr) elevates from (0.235 to 1.489) × 10−2 and (0.12 to 0.27) × 10−2 emu/g while Coercivity (Hc) reduced from 97 to 36 Oe with enhancement in the concentration of dopants in ZnO matrix. Oxygen vacancies were found to be the main reason for room-temperature ferromagnetism (RTFM) in the doped and co-doped ZnO NPs. The results show that the enhanced dielectric and magnetic properties of Mn doped and (Mn, Co) co-doped ZnO is strongly correlated with the concentration of oxygen vacancies. The observed enhanced RTFM, dielectric properties and electrical conductivity makes TM doped ZnO nanoparticles suitable for spintronics, microelectronics and optoelectronics based applications.

Experimental and theoretical evidence for the presence of room temperature ferromagnetism in undoped and Mn doped tetragonal ZrO2 nanostructures

Evidence Of The Defect-Induced Ferromagnetism In Na And Co Codoped Zno

Effect of Defects on Room-Temperature Ferromagnetism in Co and Na Co-Doped ZnO

Reconsidering the possibility of room temperature ferromagnetism in Mn doped Zirconium oxide

Absence of Ferromagnetism in Mn-doped Tetragonal Zirconia

Zn vacancy induced ferromagnetism in K doped ZnO

Zn Vacancy Induced Room-Temperature Ferromagnetism in Mn-Doped Zno

Reproducibility of room temperature ferromagnetism in Zn0.95Mn0.05O and its understanding

Experimental and Theoretical Analyses of Zinc-Vacancy-Induced Room-Temperature Ferromagnetism in ZnO Films

Magnetism and Energetics Ofmn-Dopedzno(10

Origin of Ferromagnetism in Zn-doped SnO2 from First-Principles Study

Effects of temperature on the ferromagnetism of Mn-doped ZnO nanoparticles and Mn-related Raman vibration

Search for Origin of Room Temperature Ferromagnetism Properties in Ni-Doped ZnO Nanostructure

Room-temperature ferromagnetic half metal in (C, Mn) co-doped orthorhombic ZnO with large magneto-crystalline anisotropy energy

Activation of Room-Temperature Ferromagnetism in Mn Doped Zno Thin Films by N Codoping

Confirmation of Room Temperature Ferromagnetism for Mn-doped ZnO Micro-Tetrapod Powders

Search for Origin of Room Temperature Ferromagnetism Properties in Ni doped ZnO Nanostructure

Room-temperature Ferromagnetism in Un-Doped ZrO2 Thin Films

Influence of oxygen vacancies on the structural, dielectric, and magnetic properties of (Mn, Co) co-doped ZnO nanostructures

Magnetism And Energetics Of Mn-Doped Zno (10(1)Over-Bar0) Thin Films

Influences of the Type of Dopant and Substrate on Ferromagnetism in ZnO:Mn