Abstract:Zinc (Zn) alloys are a promising biodegradable material for vascular stent applications. This study aimed to fabricate biodegradable Zn-2.0Cu-0.5Mn alloy micro-tubes and vascular stents with high dimensional accuracy and suitable mechanical properties, and to investigate their microstructure, texture, mechanical properties and corrosion behavior. The micro-tubes and vascular stents were successfully fabricated by a combined process of extrusion, drawing, laser cutting and electrochemical polishing. The microstructures of as-extruded and as-drawn micro-tubes consisted of Zn matrix with near-equiaxed grains (average grain size: ∼2 µm) and second phases of ε (CuZn4) and MnZn13 with different sizes. The texture evolved from basal planes approximately paralleling to deformation direction for as-extruded micro-tube to approximately perpendicular to deformation direction for as-drawn micro-tube, because predominant deformation mechanisms changed from basal <a> dislocation slip during tube extrusion to prismatic <a> dislocation, pyramidal <c+a> dislocations, and {101¯2} twins during tube drawing. As-drawn micro-tube exhibited suitable mechanical properties with an ultimate tensile strength of about 298 MPa and elongation of about 26% as a stent material. Moreover, the processed stent with a thickness of about 125 µm possessed sufficient radial strength of about 150 kPa and good balloon expandability. In addition, as-drawn tube exhibited an in vitro corrosion rate of about 158 µm/year with a basically uniform corrosion morphology. These results indicated that biodegradable Zn-2.0Cu-0.5Mn alloy is a promising vascular stent material candidate, and the procedure for processing the micro-tube and stent is practical and effective. STATEMENT OF SIGNIFICANCE: Fabrication of micro-tubes followed by laser cutting and polishing is a common way to prepare metallic vascular stents. However, it is quite challenging to fabricate Zn-based stents using this standard method, and there is a lack of studies reporting processing details in the past. Biodegradable Zn-2.0Cu-0.5Mn alloy micro-tubes and vascular stents with high dimensional accuracy and suitable mechanical properties were successfully fabricated by a combined process in this study. As-drawn micro-tube exhibited an ultimate tensile strength of about 298 MPa and elongation of about 26%. The stent possessed sufficient radial strength of about 150 kPa and good balloon expandability. We demonstrated a practical method to fabricate biodegradable Zn-based micro-tubes and stents with high dimensional accuracy and mechanical properties.

Microstructure and texture evolution of fine-grained Mg-Zn-Y-Nd alloy micro-tubes for biodegradable vascular stents processed by hot extrusion and rapid cooling

The processing of Mg alloy micro-tubes for biodegradable vascular stents

Forming of Magnesium Alloy Microtubes in the Fabrication of Biodegradable Stents

The deteriorated degradation resistance of Mg alloy microtubes for vascular stent under the coupling effect of radial compressive stress and dynamic medium

Enhanced plasticity of magnesium alloy micro-tubes for vascular stents by double extrusion with large plastic deformation

Fabrication and characterization of biodegradable Zn-Cu-Mn alloy micro-tubes and vascular stents: Microstructure, texture, mechanical properties and corrosion behavior

Multipass cold drawing of magnesium alloy minitubes for biodegradable vascular stents.

Microstructural Characteristics and Mechanical Properties of the Hot Extruded Mg-Zn-Y-Nd Alloys

Influence of fine-grain and solid-solution strengthening on mechanical properties and in vitro degradation of WE43 alloy

Microstructure, texture, and mechanical properties of Mg–4Zn–1Mn–xCa alloys and the fabrication of biomedical Mg thin-walled micro-tubes

Optimizing Mechanical Property and Cytocompatibility of the Biodegradable Mg-Zn-Y-Nd Alloy by Hot Extrusion and Heat Treatment

Optimization of Microstructure and Mechanical Property of a Mg-Zn-Y-Nd Alloy by Extrusion Process

Microstructure, Mechanical Properties, in Vitro Degradation and Cytotoxicity Evaluations of Mg–1.5Y–1.2Zn–0.44Zr Alloys for Biodegradable Metallic Implants

Controlled Grain Refinement of Biodegradable Zn-Mg Alloy: The Effect of Magnesium Alloying and Multi-Pass Hydrostatic Extrusion Preceded by Hot Extrusion

Enhanced Bioactivity of Mg-Nd-Zn-Zr Alloy Achieved with Nanoscale MgF2 Surface for Vascular Stent Application.

Research on Hot Extrusion and Cold Drawing for Micro-Tube of Magnesium Alloys

Effect of extrusion process on the mechanical and in vitro degradation performance of a biomedical Mg-Zn-Y-Nd alloy

Microstructure, Mechanical Properties and Creep Behaviour of Extruded Zn-xLi (x = 0.1, 0.3 and 0.4) Alloys for Biodegradable Vascular Stent Applications

Nanophasic Biodegradation Enhances the Durability and Biocompatibility of Magnesium Alloys for the Next-Generation Vascular Stents.

Microstructure, Mechanical Properties, Corrosion Behavior and Biocompatibility of As-Extruded Biodegradable Mg–3Sn–1Zn–0.5Mn Alloy

Degradation behaviors and in-vivo biocompatibility of a rare earth- and aluminum-free magnesium-based stent