Enhanced Corrosion Resistance and Biocompatibility of Mg-Zn-Y-Nd Alloy Achieved with APTES Pre-Treatment for Drug-Eluting Vascular Stent Application
Liu Jing,Xi Tingfei,Chen Ming
DOI: https://doi.org/10.3389/conf.fbioe.2016.01.01744
IF: 5.7
2016-01-01
Frontiers in Bioengineering and Biotechnology
Abstract:Event Abstract Back to Event Enhanced corrosion resistance and biocompatibility of Mg−Zn−Y−Nd alloy achieved with APTES pre-treatment for drug-eluting vascular stent application Jing Liu1, Tingfei Xi1 and Ming Chen2 1 Peking University, Academy for Advanced Interdisciplinary Studies, China 2 Peking University First Hospital, Cardiovascular Internal Medicine Department, China Bioabsorbable magnesium alloys (Mg) are advantageous in temporary functional implant applications, as they avoid the risks posed by permanent metallic implants. Nevertheless, the over-fast corrosion of Mg alloys under physiological conditions hinders its wider use as medical implants. Here we introduce a convenient one-step process to introduce a cross-linked 3-amino-propyltrimethoxysilane (APTES) silane physical barrier layer on the surface of Mg-Zn-Y-Nd alloys before coating with drug-eluting poly (glycolide-co-lactide) (PLGA) layer loaded with rapamycin. Surface microstructure was characterized by scanning electron microscope (SEM), Fourier transform infrared spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS). Nano-scratch test verifies the adhesion strength of the PLGA pre-treated with APTES is superior to direct PLGA coating. Electrochemical testing combined with long-term immersion results indicate that the APTES coating results in preferable in vitro anti-corrosion behaviour. Cell morphology and proliferation tests demonstrate that APTES pre-treated Mg-Zn-Y-Nd substrate shows markedly preferable effects for both human umbilical vein endothelial cells (EA. hy926) and vascular smooth muscle cells (VSMC). Furthermore, the in vivo test via implanting APTES pre-treated Mg-Zn-Y-Nd stent to porcine coronary arteries for 6 months confirms benign tissue compatibility with the well re-endothelialized vessel with no sign of obvious thrombogenesis and restenosis. National Basic Research Program of China (Grant No. 2012CB619102); Shenzhen Science and Technology Funding Projects (CXZZ20140730091722497); Shenzhen Special Funds for Development of Strategic Emerging Industries(Project No. JCYJ20130402172)References:[1] B. Heublein, R. Rohde, V. Kaese, M. Niemeyer, W. Hartung, A. Haverich, Heart 89 (2003) 651-656.[2] X. Liu, Z. Yue, T. Romeo, J. Weber, T. Scheuermann, Acta Biomater. 9 (2013) 8671-8677.[3] R. Erbel, C. Di Mario, J. Bartunek, J. Bonnier, B. de Bruyne, The Lancet 369 (2007) 1869-1875.[4] J. Liu, X.L. Liu, T.F. Xi, C.C. Chu, J. Mater. Chem. B. 3 (2015) 878-893.[5] F. Wittea, J. Fischera, J. Nellesenb, H.A. Crostackb, Biomaterials 27 (2006) 1013-1018. Keywords: in vivo, Biocompatibility, Surface modification, Biodegradable metal Conference: 10th World Biomaterials Congress, Montréal, Canada, 17 May - 22 May, 2016. Presentation Type: Poster Topic: Biomaterials for cardiovascular applications, vascular grafts and embolic devices Citation: Liu J, Xi T and Chen M (2016). Enhanced corrosion resistance and biocompatibility of Mg−Zn−Y−Nd alloy achieved with APTES pre-treatment for drug-eluting vascular stent application. Front. Bioeng. Biotechnol. Conference Abstract: 10th World Biomaterials Congress. doi: 10.3389/conf.FBIOE.2016.01.01744 Copyright: The abstracts in this collection have not been subject to any Frontiers peer review or checks, and are not endorsed by Frontiers. They are made available through the Frontiers publishing platform as a service to conference organizers and presenters. The copyright in the individual abstracts is owned by the author of each abstract or his/her employer unless otherwise stated. Each abstract, as well as the collection of abstracts, are published under a Creative Commons CC-BY 4.0 (attribution) licence (https://creativecommons.org/licenses/by/4.0/) and may thus be reproduced, translated, adapted and be the subject of derivative works provided the authors and Frontiers are attributed. For Frontiers’ terms and conditions please see https://www.frontiersin.org/legal/terms-and-conditions. Received: 27 Mar 2016; Published Online: 30 Mar 2016. Login Required This action requires you to be registered with Frontiers and logged in. To register or login click here. Abstract Info Abstract The Authors in Frontiers Jing Liu Tingfei Xi Ming Chen Google Jing Liu Tingfei Xi Ming Chen Google Scholar Jing Liu Tingfei Xi Ming Chen PubMed Jing Liu Tingfei Xi Ming Chen Related Article in Frontiers Google Scholar PubMed Abstract Close Back to top Javascript is disabled. Please enable Javascript in your browser settings in order to see all the content on this page.