Enabling high-performance all-solid-state lithium batteries with high ionic conductive sulfide-based composite solid electrolyte and ex-situ artificial SEI film

Jingguang Yi,Dan Zhou,Yuhao Liang,Hong Liu,Haifang Ni,Li-Zhen Fan
DOI: https://doi.org/10.1016/j.jechem.2020.09.038
IF: 13.1
2021-07-01
Journal of Energy Chemistry
Abstract:<p>All-solid-state lithium batteries (ASSLBs) employing sulfide electrolyte and lithium (Li) anode have received increasing attention due to the intrinsic safety and high energy density. However, the thick electrolyte layer and lithium dendrites formed at the electrolyte/Li anode interface hinder the realization of high-performance ASSLBs. Herein, a novel membrane consisting of Li<sub>6</sub>PS<sub>5</sub>Cl (LPSCl), poly(ethylene oxide) (PEO) and Li-salt (LiTFSI) was prepared as sulfide-based composite solid electrolyte (LPSCl-PEO3-LiTFSI) (LPSCl:PEO = 97:3 wt/wt; EO:Li = 8:1 mol/mol), which delivers high ionic conductivity (1.1 × 10<sup>−3</sup> S cm<sup>−1</sup>) and wide electrochemical window (4.9 V <em>vs.</em> Li<sup>+</sup>/Li) at 25 °C. In addition, an <em>ex-situ</em> artificial solid electrolyte interphase (SEI) film enriched with LiF and Li<sub>3</sub>N was designed as a protective layer on Li anode (Li(SEI)) to suppress the growth of lithium dendrites. Benefiting from the synergy of sulfide-based composite solid electrolyte and <em>ex-situ</em> artificial SEI, cells of S-CNTs/LPSCl-PEO3-LiTFSI/Li(SEI) and Al<sub>2</sub>O<sub>3</sub>@LiNi<sub>0.5</sub>Co<sub>0.3</sub>Mn<sub>0.2</sub>O<sub>2</sub>/LPSCl-PEO3-LiTFSI/Li(SEI) are assembled and both exhibit high initial discharge capacity of 1221.1 mAh g<sup>−1</sup> (135.8 mAh g<sup>−1</sup>) and enhanced cycling stability with 81.6% capacity retention over 200 cycles at 0.05 C (89.2% over 100 cycles at 0.1 C). This work provides a new insight into the synergy of composite solid electrolyte and artificial SEI for achieving high-performance ASSLBs.</p>
chemistry, physical,engineering, chemical, applied,energy & fuels
What problem does this paper attempt to address?
The main objective of this paper is to develop a high-performance all-solid-state lithium-ion battery (ASSLBs), specifically by designing a novel composite solid electrolyte (CSE) and fabricating an external artificial solid electrolyte interface (SEI) film on the surface of the lithium metal anode. The proposed composite solid electrolyte in the paper consists of lithium sulfide (Li6PS5Cl, abbreviated as LPSCl), polyethylene oxide (PEO), and lithium bis(trifluoromethanesulfonyl)imide (LiTFSI). This composite material exhibits a high ionic conductivity (1.1×10^-3 S cm^-1 at 25°C) and a wide electrochemical window (4.9 V vs. Li+/Li). Furthermore, the researchers formed a SEI film rich in LiF and Li3N on the external lithium metal anode by electrochemical deposition, to suppress the growth of lithium dendrites and enhance the stability of the anode. Combining these two approaches, the researchers assembled two types of all-solid-state lithium batteries, using sulfur coated with carbon nanotubes (S-CNTs) as the cathode material and aluminum-doped nickel cobalt manganese ternary material (Al2O3@LiNi0.5Co0.3Mn0.2O2) as the cathode material. Both batteries exhibited high initial discharge capacities (1221.1 mAh g^-1 and 135.8 mAh g^-1, respectively) and excellent cycle stability (capacity retention rate of 81.6% after 200 cycles and 89.2% after 100 cycles). In summary, this study provides an effective strategy to significantly enhance the performance of all-solid-state lithium-ion batteries by optimizing the composite solid electrolyte and artificial SEI film.