Environmental Friendliness and High Performance of Multifunctional Tween 80/ZnO-Nanoparticles-Added Water-Based Drilling Fluid: An Experimental Approach
Adnan Aftab,Muhammad Ali,Muhammad Faraz Sahito,Udit Surya Mohanty,Nilesh Kumar Jha,Hamed Akhondzadeh,Muhammad Rizwan Azhar,Abdul Razak Ismail,Alireza Keshavarz,Stefan Iglauer
DOI: https://doi.org/10.1021/acssuschemeng.0c02661
2020-07-21
Abstract:The energy industry is exploring sustainable chemistry and engineering solutions for exploitation of shale reservoirs. Smectite-rich shale is challenging to drill with traditional water-based drilling fluid (WBDF). The objectives of this study are (i) to investigate acute toxicity of drilling fluids and (ii) to enhance the rheological properties, lubricity, and clay inhibition behavior of WBDF by adding Tween 80 (T80)/ZnO nanoparticles. Acute toxicity results revealed 100% survival rate of white leg shrimp in WBDF waste. At 0.7 g, the optimum concentration of T80ZnO, the plastic viscosity (PV) was improved by 12%; the negative surface charge of nanomaterial might have improved repulsion forces/stability and enhanced viscosity in the drilling fluids. Yield point (YP) was improved by 71%, moreover 10 min gel strength (GS) and 10 s GS were significantly increased by 32 and 54%, respectively. The metal oxide nanosolids induced heat transfer characteristics and ensured gelling and yield strength properties. Lubricity was slightly increased by 7%; the ZnO nanorods between the two sliding contact surfaces (i.e., assuming drill pipe and casing) improved lubricity. Filtrate loss (FL) volume was considerably minimized to 17 and 30% at API and high-pressure, high-temperature (HPHT) conditions, respectively; this observation could be explained by pores plugging in the filter paper. Heated clay swelling inhibition was optimized after addition of 0.6 g of T80ZnO nanoparticles to WBDF. The clay inhibition was enhanced by 9 and 17% when compared to conventional WBDF and fresh water, respectively; this progress might have attributed to the corresponding: (i) pores plugging in the clay and (ii) interparticle pores bridging between existing drilling additives and nanomaterial. The above findings identify that this drilling fluid could attain sustainable environmental and operational success while drilling into montmorillonite/smectite rich-clay and shale rock.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssuschemeng.0c02661.(a) Drilling fluid additives used for preparation of traditional and T80ZnO nanoparticles added drilling fluids (b) the color of mixture varied at every step (c) sedimentation test of nanomaterial added drilling fluid (Figure S1 a to c), Shrimp collection point and information regarding compliance with regulatory restrictions (Table S1), (a) Molar solution placed in oven (b) filtration of synthesized T80ZnO nanoparticles (c) collection of synthesized of T80ZnO nanoparticles into the capsules (Figure S2 a to c), T80ZnO nanofluid after sonication at variable last three high concentrations (Figure S3), Hot plate placed in the holding chamber of Fann viscometer 35SA for the measurement of rheological properties at 150 °F elevated temperature (Figure S4),. (a) Parts of API filter press (b) filter screen followed by filter paper and gasket assembled into lower cap and attached to the bottom of drilling fluid chamber(c) upper cap attached to the top of drilling fluid chamber (Figure S5 a to c), (a) FTIR of synthesized T80ZnO nanoparticles (b) median diameter of T80ZnO nanoparticles (c) TEM of T80ZnO nanoparticles yellowish solution at 200 nm scale shows no agglomeration (Figure S6 a to c), (a) XRD of clay1 (b to e) FESEM of clay and measurement of pore sizes (Figure S7), mineralogy and weight percent of API bentonite (Table S2), (a) Heated clay pellet immersed in 140 ml of water (b) heated clay pellet immersed in 140 ml of conventional WBDF (c) heated clay immersed in 0.1 % of synthesized T80ZnO nanoparticles water (Figure S8a to d), effectiveness of T80ZnO added drilling fluid in enhancing the rheological properties, filtrate loss, lubricity, and clay inhibition relative to last 5 years published technical literature on water based drilling fluid (Table S3) (PDF)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology