Abstract:It is well established that fatigue crack nucleation and small crack growth in high strength aluminum alloys are highly influenced by the surrounding microstructure including grain boundaries, texture, inclusion barriers, among other factors. As such, specific and targeted experimental and computational methods are necessary to accurately capture and predict the discrete behavior of microstructurally small fatigue cracks. In this study, surface fatigue crack nucleation and microstructurally small crack growth in high strength aluminum alloys, commonly used in aerospace applications, are evaluated through a holistic approach encompassing fatigue testing, crack measurement, and computational prediction of crack growth rates. During fatigue testing, crack shapes and growth are quantified using a novel surface replication technique that is applied to investigate crack nucleation, as well as to collect validation data that includes an accurate description of crack shape during crack propagation, a challenging and essential component in predicting crack growth. Computational simulation of fatigue crack growth in non-straight, complex surface crack arrays typically requires high fidelity analysis using computationally expensive methods to account for the mathematical and geometrical complexities inherent in the solution. A dislocation distribution based technique has been previously demonstrated to rapidly and accurately predict the stress intensity factors for through cracks of complex shape. This method was expanded and investigated as an approach for rapidly predicting the crack growth rate of kinked and tortuous surface crack arrays, using the crack configuration and bulk material properties as inputs. To investigate the accuracy and effectiveness of this characterization approach, surface crack growth in AA7075-T7351 was experimentally analyzed and modeled under high cycle and low cycle fatigue conditions. This comprehensive approach was determined to be an expedient and applicable method for characterizing and evaluating the nucleation and crack growth rate of non-planar microstructurally small and short crack configurations.

Self-organized criticality as a precursor of fatigue: application to shape memory alloys

Microstructural mechanisms of cyclic deformation, fatigue crack initiation and early crack growth

Fatigue life prediction at mesoscopic scale of samples containing casting defects: A novel energy based non-local model

Criticality in the approach to failure in amorphous solids

Failure modes of complex materials with spatially-correlated mechanical properties -- the critical role of internal damage

Computational Monitoring of an Initial Fatigue Crack Incubation and Growth in a Smooth Specimen

Fatigue failure in glasses under cyclic shear deformation

A Mathematical Model for Competing Failure Modes in Strain Cycle Fatigue

Computer simulation of fatigue under diametrical compression

Fatigue fracture mechanism of amorphous materials from a density-based coarse-grained model

The heterogeneity of persistent slip band nucleation and evolution in metals at the micrometer scale

Fatigue Life and Mechanistic Modeling of Interior Micro-Defect Induced Cracking in High Cycle and Very High Cycle Regimes

Prediction of Low Cycle Fatigue Crack Growth under Mixed-mode Loading Conditions Using Cohesive Zone Models

Characterization of Surface Fatigue Crack Nucleation and Microstructurally Small Crack Growth in High Strength Aluminum Alloys

Probabilistic modeling and simulation of multiple surface crack propagation and coalescence

Failure of Metals II: Fatigue

Fatigue crack growth in anisotropic aluminium sheets -- phase-field modelling and experimental validation

Intrinsic Fatigue Limit and the Minimum Fatigue Crack Growth Threshold

Damage spreading in quasi-brittle disordered solids: II. What the statistics of precursors teach us about compressive failure

Spatial Poisson processes for fatigue crack initiation

Autonomous healing of fatigue cracks via cold welding