Residual Stress Measurement Using X-ray Diffraction in Friction Stir-Welded Dissimilar Titanium Alloys

Kapil Gangwar,M Ramulu,M. Ramulu

DOI: https://doi.org/10.3390/ma17071482

IF: 3.4

2024-03-25

Materials

Abstract:Surface residual stresses in welded specimens significantly influence properties such as fatigue resistance, fracture toughness, and the superplasticity of joints. In this study, we employed friction stir welding, a well-established joining method, to weld dissimilar titanium alloys. By combining two distinct titanium alloys, we aimed to harness their unique properties when subjected to cyclic loading, impact, or superplastic forming processes. Utilizing X-ray diffraction, macroscopic surface stresses were assessed in dissimilar titanium alloys (Ti-6242 standard grain (SG) and Ti-54M) welded via friction stir welding, assuming a linear lattice distortion. The study accounted for misalignment, significant distortion, and grain refinement in the stir zone. Macroscopic surface residual stresses were quantified on the weld surface and at a depth of 1.5 mm beneath it within a square cross-section (1 × 1 mm2) by oscillating the specimen in the (X-Y) direction. The sin2φ method, implemented through the LEPTOS® (v7.8) software, was employed for residual stress measurement. The analysis of the results was conducted with respect to different rotation and traverse speeds. It was noted that at the center (CEN) of the weld, commonly referred to as the weld nugget, approximately 50 MPa of tensile stress was observed under the lowest values of both tool rotation speed and traverse speed. Tensile residual stresses were evident at the boundaries and within the stir zone. No discernible pattern was observed at the specified locations. Notably, the resultant values of residual stress, influenced by rotation and traverse speeds, exhibited asymmetry.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

This paper mainly discusses how to measure residual stresses in dissimilar titanium alloys using X-ray diffraction technique for friction stir welding (FSW). In the study, the authors combined two different types of titanium alloys through FSW in order to utilize their unique properties during cyclic loading, impact, or superplastic forming processes. Macroscopic surface stresses, especially at a square section (1×1 mm²) on the weld surface and 1.5 mm below it, were investigated using X-ray diffraction.

The paper employed the sin2φ method of LEPTOS® software to measure residual stresses and analyzed different rotational speeds and traverse speeds. The results showed the presence of approximately 50 MPa tensile stress at the center of the weld (weld nugget), as well as tensile residual stresses in the boundaries and stir zone. The study also found that the values of residual stresses were influenced by rotational and traverse speeds, exhibiting asymmetry.

The paper emphasizes the impact of residual stresses, whether compressive or tensile, on fatigue crack growth and mentions that migratory elements and severe plastic deformation can affect crystal orientation and lattice strain in dissimilar titanium alloys for FSW. Despite existing research on the same titanium alloys, there is a lack of residual stress data for dissimilar titanium alloys. Therefore, this study is of significant importance for understanding the relationship between fundamental processing parameters, such as traverse and rotational speeds, and residual stresses, as well as for applications in aerospace, automotive, and biomedical implantation fields.