The effect of additional elements on hydrogen permeation properties of melt-spun Ni-Nb-Zr amorphous alloys

S. Yamaura,Y. Shimpo,H. Okouchi,O. Kajita,M. Nishida,A. Inoue

DOI: https://doi.org/10.2320/MATERTRANS.45.330

2004-02-20

Abstract:The (Ni 0 . 6 Nb 0 . 4 ) 4 5 Zr 5 0 X 5 (X = Al, Co, Cu, P, Pd, Si, Sn, Ta or Ti) alloy ribbons were produced by the melt-spinning technique. All ribbon specimens were confirmed to have a single amorphous phase by XRD analysis. The crystallization temperatures of the melt-spun (Ni 0 . 6 Nb 0 . 4 ) 4 5 Zr 5 0 X 5 (X = Al, P, Pd, Si or Sn) amorphous alloys are higher than that of the (Ni 0 . 6 Nb 0 . 4 ) 5 0 Zr 5 0 amorphous alloy (727 K). Although the hydrogen permeability of the (Ni 0 . 6 Nb 0 . 4 ) 4 5 Zr 5 0 X 5 (X = Si, Sn, Ta or Ti) amorphous alloys could not be measured due to severe embrittlement during the permeation test, the (Ni 0 . 6 Nb 0 . 4 ) 4 5 Zr 5 0 X 5 (X = Al, Co, Cu, P or Pd) amorphous alloys had high ductility which was enough to measure the permeability. The hydrogen permeabilities of the (Ni 0 . 6 Nb 0 . 4 ) 4 5 Zr 5 0 Co 5 and the (Ni 0 . 6 Nb 0 . 4 ) 4 5 Zr 5 0 Cu 5 amorphous alloys were 2.46 × 10 - 8 and 2.34 × 10 - 8 [mol-m - 1 .s - 1 .Pa - 1 / 2 ] at 673 K, respectively. The (Ni 0 . 6 Nb 0 . 4 ) 4 5 Zr 5 0 P 5 amorphous alloypossesses the lowest permeability of 1.36 x 10 - 8 [mol.m - 1 .s - 1 .Pa - 1 / 2 ] at 673 K among the alloys where the permeability was measured. The reduction of the permeability in the (Ni 0 . 6 Nb 0 . 4 ) 4 5 Zr 5 0 P 5 amorphous alloy is thought to be due to a preferential development of Zr-P atomic pairs which may suppress hydrogen solubility and hydrogen diffusivity in the alloy, because the heat of mixing for Zr-P atomic pairs is negatively larger than those of other pairs such as Ni-P and Nb-P. It is concluded that the Ni-Nb-Zr-X (X=Co or Cu) amorphous alloys have high potential to hydrogen permeable membranes.

Materials Science