Development of Nb-based alloy membranes with improved resistance to corrosion by H 2 S
Erhu Yan,shuo Zhang,Wei Liu,Kexiang Zhang,Guanzhong Huang,Limin Jia,Lizhen Tao,Hongfei Chen,Jinwang Bai,Hailiang Chu,Yongjin Zou,Huanzhi Zhang,Fen Xu,Lixian Sun
DOI: https://doi.org/10.2139/ssrn.4675895
IF: 9.5
2024-03-30
Journal of Membrane Science
Abstract:At present, the interest in non-Pd hydrogen permeation membranes mainly focuses on group 5 B metals (Nb, V, Ta) and their alloys. To solve the problem of easy oxidation and weak dissociation of hydrogen molecules, a "Pd catalytic layer" needs to be deposited on the membrane surface. Due to its limited stability towards sulfur, issues of irreversible poisoning by sulfur compounds must be addressed. To this end, Pd-, Pd 65 Ag 35 -, Pd 90 Cu 10 -, Pd 80 Au 20 -, and Pd 55 Ag 35 Au 10 -coated Nb 30 Hf 35 Co 35 membranes were firstly synthesised by magnetron sputtering, and their hydrogen permeation behaviour in pure H 2 and/or in different H 2 /H 2 S mixtures for up to 1000 ppm at 673 K were evaluated. At these conditions, the permeabilities of the Pd-coated membranes decrease rapidly with increasing the H 2 S concentration and cannot recover after removal of H 2 S from the feed mixtures. In comparison, the Pd–Ag-containing membrane greatly increases the pure H 2 permeability, whereas the membrane doped with Au can effectively improve the response to H 2 S. Specifically, the Pd 65 Ag 35 -coated membrane shows the highest pure H 2 permeability, but it loses maximum permeability value on exposure to H 2 /H 2 S feed mixtures. In contrast, Pd 80 Au 20 -containing membranes exhibit good tolerance of H 2 S poisoning and displayed a high fractional recovery (∼83%) of initial H 2 permeability. The degradation of permeability for Pd- or Pd 65 Ag 35 -coated membranes after the H 2 S exposure can be ascribed to the deterioration of the structure caused by the possible formation of bulk Pd 4 S, which has been corroborated with EDS analysis, XRD, and XPS after testing. Finally, to improve both permeability and chemical tolerance, a Pd 55 Ag 35 Au 10 -coated membrane was successfully fabricated, and it possesses excellent comprehensive performance with respect to the permeability and H 2 S response. At 120 ppm H 2 S in the feed, the H 2 flux equals ca. 43% of its original value at 673 K and can be stable for at least 166 h. Bulk sulfides did not form on the membrane surface after the testing. This paper not only developed a new type of group 5 B alloy membrane with improved resistance to corrosion by H 2 S, but also further confirmed the feasibility of improving H 2 S corrosion resistance by adjusting the catalytic layer type or composition of the outermost coating.
engineering, chemical,polymer science