Abstract:Cu and unoxidized graphene composite films were prepared by electroplating under room temperature. Graphene was added to the electrolyte of Cu to form composite materials to improve the performance of Cu for interconnection. Composite electrolyte containing high concentration of graphene (up to 0.5 g/L) was prepared by adding CTAB as surfactant. And ultrasound was also used to increase dispersion degree and reduce graphene agglomeration in electrolyte. Average coefficient of thermal expansion (CTE) of the composite films determined by thermo-mechanical analysis (TMA) shows a decrease from 17.3 ppm/K to 14.2 ppm/K from 260 K to 320 K, which reduce CTE by 18 % compared with Cu. CTE of the composite materials can be reduced to 10 ppm/K at 243 K, which is only 60 % of CTE of Cu. The thermal conductivity of the composite materials measured by phase sensitive transient thermo-reflectance (PSTTR) technique shows an improvement from 385 W/m.K to 468 W/m.K. CTE and thermal conductivity of the composite materials both decrease with the increase of current density. And they also both increase with the increase of graphene concentration. The composite materials also show good mechanical properties. The average hardness is 2.5 GPa, which is about 2 times of Cu. And the average elastic modulus is 145 GPa, which is 38 % higher than that of Cu. The resistivity of the composite materials is basically equivalent to that of pure Cu. Result of the experiment proved that the composite materials have better performance under low temperature conditions. The improvement of material properties makes composite materials have good application prospects for 3D interconnection in the near future.

Preparation and Properties of Cu-Plated Graphene/Cu Composites

Microstructure and Nanoindentation Behavior of Cu Composites Reinforced with Graphene Nanoplatelets by Electroless Co-Deposition Technique

Bulk graphene-based composites with artificial nacre-like laminated structure: Microstructure and mechanical properties

A novel approach to fabricate layered RGO/Cu composites with excellent mechanical properties

Graphene-copper Composite with Micro-Layered Grains and Ultrahigh Strength

Preparation and Characterization of Electroplated Cu/Graphene Composite

Preparation and Mechanical Property of Graphene-reinforced Copper Matrix Composites

Enhancement of Thermal Conductivity and Mechanical Properties of Cu-Reduced Graphene Oxide Composites by Interface Modification

Facile Preparation of High-Performance Reduced Graphene Oxide (RGO)/Copper (Cu) Composites Based on Pyrolysis of Copper Formate

Characterization and Tribological Properties of Graphene/Copper Composites Fabricated by Electroless Plating and Powder Metallurgy

Preparation of graphene nanoplatelets-copper composites by a modified semi-powder method and their mechanical properties

Effect of reduced graphene oxide nanoplatelets content on the mechanical and electrical properties of copper matrix composite

Preparation and properties of Cu/RGO composites via H2 reduction and spark plasma sintering

Preparation and properties of graphene reinforced Cu/0.5CeO230Cr electrical contact materials

Mechanical and Electrical Properties of Graphene Oxide Reinforced Copper–Tungsten Composites Produced via Ball Milling of Metal Flakes

W-Cu Composites Reinforced by Copper Coated Graphene Prepared Using Infiltration Sintering and Spark Plasma Sintering: A Comparative Study

Preparation of graphene/copper composites using solution-combusted porous sheet-like cuprous oxide

Research on the performance of rGO-CNTs synergistically enhanced copper matrix composites

Effect of Copper-Plated Graphite Content on the Microstructure and Properties of Copper-Graphite Composites Prepared by Spark Plasma Sintering

Microstructure and Properties of a Graphene Reinforced Cu–Cr–Mg Composite

laminated Cu-GO-Cu composite foils with improved mechanical and thermal properties by alternating DC electro-deposition and electrophoresis