Abstract:Due to the non-uniform distribution of meso-structure, the diffusion of chloride ions in concrete show the characteristics of characteristics of randomness and fuzziness, which leads to the non-uniform distribution of chloride ions and the non-uniform corrosion of steel rebar in concrete. This phenomenon is supposed as the main reason causing the uncertainty of the bearing capacity deterioration of reinforced concrete structures. In order to analyze and predict the durability of reinforced concrete structures under chloride environment, the random features of chloride ions transport in concrete were studied in this research from in situ meso-structure of concrete. Based on X-ray CT technology, the spatial distribution of coarse aggregates and pores were recognized and extracted from a cylinder concrete specimen. In considering the influence of ITZ, the in situ meso-structure of concrete specimen was reconstructed to conduct a numerical simulation on the diffusion of chloride ions in concrete, which was verified through electronic microprobe technology. Then a stochastic study was performed to investigate the distribution of chloride ions concentration in space and time. The research indicates that the influence of coarse aggregate on chloride ions diffusion is the synthetic action of tortuosity and ITZ effect. The spatial distribution of coarse aggregates and pores is the main reason leading to the non-uniform distribution of chloride ions both in spatial and time scale. The chloride ions concentration under a certain time and the time under a certain concentration both satisfy the Lognormal distribution, which are accepted by Kolmogorov-Smirnov test and Chi-square test. This research provides an efficient method for obtain mass stochastic data from limited but representative samples, which lays a solid foundation for the investigation on the service properties of reinforced concrete structures.

Spatiotemporal interpolation of surface chloride content for marine RC structures based on non-uniform spatiotemporal Kriging interpolation method

Influence of Stochastic Chlorine Environment on the Spatiotemporal Deterioration of Marine RC Structures

CONCRETE SURFACE CHLORIDE ION CONCENTRATION VARYING WITH HEIGHT IN MARINE ENVIRONMENT

Statistic Investigation on Chloride Ions Distribution Based on Numerical Reconstruction of in Situ Meso-Structure of Concrete

Durability related environmental zonation and design methodology for marine RC structures

Chloride Ion Ingress Distribution Within an Alternate Wetting-Drying Marine Environment Area

Spatial Variability-Based Corrosion Risk Assessment and Strategy of Repair and Maintenance for RC Structures

Chloride penetration in concrete under marine atmospheric environment – analysis of the influencing factors

Service Life Evaluation of Marine Concrete Structures Considering Spatial and Temporal Characteristics: A Framework Based on Multi Training-Mcs-nls

Effect of Aggregates Spatial Distribution on Three-Dimensional Transport of Chloride Ions in Reinforced Concrete

Seasonal Variation of Surface Chloride Ion Content and Chloride Diffusion Coefficient in A Concrete Dock

Stochastic investigation on three-dimensional diffusion of chloride ions in concrete

Probabilistic evaluation of chloride ingress process in concrete structures considering environmental characteristics

Data-driven Corrosion Failure Probabilistic Assessment Model for Reinforced Concrete Structures

SIMULATED RESEARCH ON CORROSION OF REINFORCEMENT IN CONCRETE UNDER CHLORIDE ENVIRONMENT

Study on the Real-Time Dynamic Monitoring of Corrosion Rate of Reinforcement in Carbonation Environment

A New Test Method to Simulate Chloride Penetration into Concrete in Tidal Zone

Peak Value Distribution of Surface Chloride Concentration and Convection Depth of Concrete

A New Corrosion Sensor To Determine The Start And Development Of Embedded Rebar Corrosion Process At Coastal Concrete

Service life prediction of RC structures in marine environment using long term chloride ingress data: Comparison between exposure trials and real structure surveys

Dynamic Self-Balanced Electrochemical Model for Non-Uniform Corrosion of Steel Reinforcement in Concrete under Combined Effects of Heat-Moisture-chlorine-oxygen