Abstract:The advantages of utilizing activated carbonate additions as a surplus provider of calcium were elucidated in this study. The pozzolanic activity inherent in clays and minerals containing carbonate can be tailored through the de‐hydroxylation of clay and the de‐carbonation of calcite content. Special consideration needs to be given to ensuring the effective activation of schist‐type materials, given the potential for substantial variations between the outcomes of laboratory‐scale and industrial‐scale activation processes for materials characterized by very low thermal conductivity, such as schists. Supplementary cementitious materials (SCMs) are partial substitutes for ordinary Portland cement (OPC) to reduce cost, the production of carbon dioxide (CO2), and fossil fuel consumption. Recent studies illustrated the effectiveness of calcined kaolinite clay as a proper partial replacement for OPC. Hence, schist‐type materials containing sufficient clay contents are regarded as promising candidates for OPC replacement. This study focuses on the possible use of activated calcium carbonates (CaCO3) to augment pozzolanic reactions of schists as a substitute for OPC. The use of activated calcium carbonates proved to be successful in expediting pozzolanic reactions and facilitating the formation of additional calcium aluminosilicate hydrate (C‐A‐S‐H). In this study, the optimal strength performance for blended cement was achieved by adjusting the total carbonate content to 30 wt.% of the schist. The decision to introduce carbonate to the schist was guided by calculations determining the need for an excess of calcium ions to fully harness the potential for C‐A‐S‐H formation. Virgin and augmented schists were activated by up to 80% of their respective potentials by heat treatment. Phase content and decomposition behavior of the active components were investigated by thermogravimetric analysis (TGA), x‐ray diffraction (XRD), and scanning electron microscopy (SEM). Cement paste samples incorporating 30 wt.% replacement of OPC with activated schist SCMs were prepared. The phase distribution and compressive strengths of these samples were assessed at hydration intervals of 2, 7, 28, 50, and 90 days. Cement formulations with activated calcium‐augmented SCMs exhibited compressive strength values at 109%, 101%, 96%, 95%, and 94% compared to pure cement paste at 2, 7, 28, 50, and 90 days, respectively. These values surpassed 90% of the compressive strength of pure OPC at equivalent hydration time points.

Exploring sulfate optimization techniques in Limestone Calcined Clay Cements (LC3): limitations and insights

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Optimization of Formula for Stabilizing Muddy Soil Using Response Surface Methodology

A Fresh View on Limestone Calcined Clay Cement (LC3) Pastes

Influence of C–S–H seed and sodium sulfate on the hydration and strength of limestone calcined clay cement

Performance of Limestone Calcined Clay Cement (LC3) with various kaolinite contents with respect to chloride transport

In situ synchrotron powder diffraction study of LC 3 cement activation at very early ages by C-S-H nucleation seeding

Investigating the sulfate resistance of mortars with multiple mineral admixtures in ammonium-magnesium sulfate solution

Early Strength-Promoting Mechanism of Inorganic Salts on Limestone-Calcined Clay Cement

Portland/Sulfoaluminate Cement Blends for the Control of Early Age Hydration and Yield Stress

The Synergistic Effect of Calcained Coal-Series Kaolinite and Limestone on the Hydration of Portland Cement

Limestone Calcined Clay as Potential Supplementary Cementitious Material—An Experimental Study

Optimization of Ca/Si ratio in schists to enhance the pozzolanic supplementary cementitious material for OPC blending

Study on the Influence of Thermoplastic Microcapsules on the Sulfate Resistance and Self-Healing Performance of Limestone Calcined Clay Cement Concrete

Microstructural investigation and performance of LC3 cementitious materials

Evaluation of the Durability of Concrete with the Use of Calcined Clays and Limestone in Salinas, Ecuador

The Effect of μ-Limestone Additions on the Mechano-Chemical and Microstructural Properties of Slag and Binary Slag/Ground Fly Ash Alkaline-Activated Binders

Use of spent fluid catalytic cracking catalyst (FCC) in Limestone Calcined Clay Cement (LC3) systems: Studies in pastes and mortars

Blast furnace slag supersulfated cements: composition optimization, microstructures, and environmental impact

Transformations in the reaction products and properties of carbonation-cured CSA cements exposed to a sulfate attack

MgO-based supersulfated cement with different industrial by-product gypsum: Experiments and molecular dynamics simulation