Abstract:Portland cements (PCs) and cement blends are multiphase materials of different fineness, and quantitatively analysing their hydration pathways is very challenging. The dissolution (hydration) of the initial crystalline and amorphous phases must be determined, as well as the formation of labile (such as ettringite), reactive (such as portlandite) and amorphous (such as calcium silicate hydrate gel) components. The microstructural changes with hydration time must also be mapped out. To address this robustly and accurately, an innovative approach is being developed based on in situ measurements of pastes without any sample conditioning. Data are sequentially acquired by Mo Kα1 laboratory X-ray powder diffraction (LXRPD) and microtomography (µCT), where the same volume is scanned with time to reduce variability. Wide capillaries (2 mm in diameter) are key to avoid artefacts, e.g. self-desiccation, and to have excellent particle averaging. This methodology is tested in three cement paste samples: (i) a commercial PC 52.5 R, (ii) a blend of 80 wt% of this PC and 20 wt% quartz, to simulate an addition of supplementary cementitious materials, and (iii) a blend of 80 wt% PC and 20 wt% limestone, to simulate a limestone Portland cement. LXRPD data are acquired at 3 h and 1, 3, 7 and 28 days, and µCT data are collected at 12 h and 1, 3, 7 and 28 days. Later age data can also be easily acquired. In this methodology, the amounts of the crystalline phases are directly obtained from Rietveld analysis and the amorphous phase contents are obtained from mass-balance calculations. From the µCT study, and within the attained spatial resolution, three components (porosity, hydrated products and unhydrated cement particles) are determined. The analyses quantitatively demonstrate the filler effect of quartz and limestone in the hydration of alite and the calcium aluminate phases. Further hydration details are discussed.

In situ synchrotron powder diffraction study of LC 3 cement activation at very early ages by C-S-H nucleation seeding

Mix and measure II: joint high-energy laboratory powder diffraction and microtomography for cement hydration studies

Influence of C–S–H seed and sodium sulfate on the hydration and strength of limestone calcined clay cement

Early Strength-Promoting Mechanism of Inorganic Salts on Limestone-Calcined Clay Cement

Microstructural investigation and performance of LC3 cementitious materials

A Fresh View on Limestone Calcined Clay Cement (LC3) Pastes

Early Hydration and Viscoelastic Properties of Tricalcium Aluminate Pastes Influenced by Soluble Sodium Salts

Improving the Early Age Strength of Eco-Efficient Mortar with Low Clinker Content Considering Binder Granulometry and Chemical Additives

In Situ Soft X-ray Spectromicroscopy of Early Tricalcium Silicate Hydration

Exploring sulfate optimization techniques in Limestone Calcined Clay Cements (LC3): limitations and insights

13C, 27Al and 29Si NMR Investigation of the Hydration Kinetics of Portland-Limestone Cement Pastes Containing CH3-COO−-R+ (R=H or Na) Additives

The Synergistic Effect of Calcained Coal-Series Kaolinite and Limestone on the Hydration of Portland Cement

Xonotlite and Hillebrandite as Model Compounds for Calcium Silicate Hydrate Seeding in Cementitious Materials

Evaluation of the Durability of Concrete with the Use of Calcined Clays and Limestone in Salinas, Ecuador

Design and characterization of iron–calcium–aluminium–silicate–hydrate as low-temperature binder

Chloride binding behaviors and early age hydration of tricalcium aluminate in chloride-containing solutions

Use of spent fluid catalytic cracking catalyst (FCC) in Limestone Calcined Clay Cement (LC3) systems: Studies in pastes and mortars

Calorimetric Study of Ternary Binder of Calcium Aluminate Cement, Portland-limestone Cement and FGD Gypsum

Early Hydration Heat of Calcium Sulfoaluminate Cement with Influences of Supplementary Cementitious Materials and Water to Binder Ratio

The Effect of μ-Limestone Additions on the Mechano-Chemical and Microstructural Properties of Slag and Binary Slag/Ground Fly Ash Alkaline-Activated Binders

The influence of low calcium sulfate contents on early calcium aluminate cement–calcite hydration kinetics and pore solution chemistry