The formation mechanism of metal-ceramic interlayer interface during laser powder bed fusion

Liming Yao,Zhongmin Xiao,Sheng Huang,Upadrasta Ramamurty
DOI: https://doi.org/10.1080/17452759.2023.2235324
IF: 10.6
2023-08-04
Virtual and Physical Prototyping
Abstract:Experiments on Laser powder bed fusion (LPBF) of powdered Ti on Al 2 O 3 substrate were conducted and the interface formation was studied using a multi-material fluid dynamics model. Results show that the melt pool is relatively shallow, with relatively flat interlayer interface under LPBF's conduction mode. In this condition, a thin sheath of molten Al 2 O 3 forms and acts as a lubricating film for the molten Ti, leading to Rayleigh instability due to high flow inertia. Keyhole formation penetrates the Al 2 O 3 substrate, resulting in a wavy interlayer interface. The recoil pressure from the keyhole and overall melt inertia are suppressed by the highly viscous molten Al 2 O 3 , thereby improving single-track melt pool stability. However, the thermal expansion coefficient difference between Ti and Al 2 O 3 led to the formation of transverse cracks. Achieving a defect-free metal-on-ceramic single track remains a challenge, despite this study serving as a guide for melt track and interface control.
engineering, manufacturing,materials science, multidisciplinary
What problem does this paper attempt to address?