High-Performing and Fire-Resistant Biobased Epoxy Resin from Renewable Sources
Jinyue Dai,Yunyan Peng,Na Teng,Yuan Liu,Chuanchuan Liu,Xiaobin Shen,Sakil Mahmud,Jin Zhu,Xiaoqing Liu
DOI: https://doi.org/10.1021/acssuschemeng.8b00439
2018-05-16
Abstract:Epoxy resins with high thermal and mechanical performance as well as good resistance to fire are difficult to synthesize. In this work, a high-performance intrinsically flame-retardant epoxy resin (diglycidyl ether of daidzein (DGED)) was synthesized from renewable daidzein using an efficient one-step process, without the addition of additional flame retardants. The structure of DGED was confirmed by Fourier transform infrared (FTIR), 1H NMR, and 13C NMR before it was cured with 4,4′-diaminodiphenylmethane (DDM). A commercial diglycidyl ether of bisphenol A (DGEBA) was cured with the same curing agent. Results indicated that the cured DGED/DDM system possessed glass transition temperature (T g) of up to 205 °C (172 °C for DGEBA/DDM), and tensile strength, tensile modulus, flexural strength, and flexural modulus of 83, 2972, 131, and 2980 MPa, respectively, all much higher than those of cured DGEBA/DDM. The cured DGED/DDM system demonstrated excellent flame-retardant properties, showing a residual char of 42.9% at 800 °C, limiting oxygen index (LOI) of 31.6%, and flammability rating of V-0 in UL94 test. This work provides us an efficient method to prepare high-performance epoxy resin from renewable resource.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology