Preparation and Electrical Life Performance of Multi-component Modified Ag/SnO2 Electrical Contact Materials by Internal Oxidation Method
Tao Shen,Chengfa Mu,Xudan Cao,Zhenwu Liu,Yue Li,Linchi Chen,Xiao Chen,Hui Yang
DOI: https://doi.org/10.12442/j.issn.1002-185x.20230204
2024-01-01
Rare Metal Materials and Engineering
Abstract:In order to explore the impact of the type and content of the modified components on the preparation process, microstructure, microhardness, temperature rise and electrical life of the modified Ag/SnO2In2O3 contact materials, the modified AgSnIn alloys were synthesized by medium-frequency smelting and casting process, and then the corresponding Ag/SnO2In2O3 contact materials were prepared by internal oxidation method. The AC-4 electrical life type testing platform was used to evaluate the temperature rise and electrical life performance of the materials. The results show that the optimum parameters of internal oxidation process of the modified Ag/SnO2In2O3 materials are 700 degree celsius/5 MPa/48 h. Compared with the binary modification of Ni, Cu or Zn, there exists larger micro-strain in the Ni-Cu-Zn ternary modified AgSn In alloys, and the microhardness of the corresponding modified Ag/SnO2In2O3 material increases first and then decreases sharply with indium content decreasing. The modified AgSn In alloy, composed of 0.47wt%Ni, 0.4wt%Cu, 0.43wt%Zn and 2.1wt%In, could achieve complete internal oxidation. The corresponding modified Ag/SnO2In2O3 material presents the optimum microhardness (1382.49 MPa), the longest cycle number (28989 operations) and an appropriate temperature rise (43.69 K), which is attributed to some larger micro-strain (1.9x10-4)-4 ) and grain boundary structure with strengthening effect. The comparison analysis reveals a positive correlation has been established between the electric life cycle number and the microhardness of the modified Ag/SnO2 2 material within In element content range from 2.1wt% to 3.1wt%, which provides a new idea for the formulation design and electric life performance prediction of the Ag/SnO2 2 contact material.