Preparation and Arcing Characteristics of Ag/SnO2 Electrical Contacts
Ma Guanglei,Zhang Lingjie,Wu Xinhe,Shen Tao,Yang Hui,Chen Xiao,Fan Xianping
2020-01-01
Rare Metal Materials and Engineering
Abstract:Using Ag powder and nano-SnO2 as raw materials, Ag/SnO2 electrical contact materials and its rivets were prepared by mechanical alloying and hot extrusion and cold press-welding process. The phase composition of the commercial Ag powder, as-prepared SnO2 and Ag/SnO2 composite powders was analyzed by X-ray diffractometry (XRD). The surface morphology and arcing characteristics and mass loss of the rivets before and after the electrical life test were characterized by scanning electron microscopy (SEM). The effects of different process parameters (working current and cycle number) on the arcing characteristics, arc eroded morphology, mass loss and degradation mode of Ag/SnO2 contacts were analyzed and compared. The results show that compared with pure Ag, Ag/SnO2 electrical contacts have higher arcing time and arcing energy under arcing, and the average arcing time of making-arc and breaking-arc is 51.78 and 25.86 ms, which is 4.87 and 2.78 ms higher than that of pure silver, respectively; the average arcing energies of making-arc and breaking-arc are 988.14 and 493.85 mJ, which are 104.93 and 58.76 mJ higher than those of pure silver, respectively. As the number of cycle operations increases, the total mass loss of the Ag/SnO2 electrical contacts is negative, and its main failure degradation modes of droplet splatter and SnO2 particles floating are manifested.