Abstract:The Ag/BiFeO3 thin films were prepared on ITO/glass substrate by in situ sol–gel method. The morphology and formation of the perovskite phase and Ag nanoparticles (NPs) were studied by XRD, SEM, and UV–Vis spectra. The doping of Ag+ ions and the formation of defects were analyzed by XPS measurement. The dielectric and magnetic properties were measured by impedance analyzer and magnetic property measurement system. Results showed that a few Ag+ ions (<7%) were doped into the bismuth ferrite lattice to substitute Bi. In addition, most of the Ag+ ions were reduced to Ag NPs in BiFeO3 thin films and the Ag NPs/BiFeO3 composite thin film was formed. The Ag+ ions doping was beneficial for not only the formation of crystalline phase of bismuth ferrite, but also the preferential orientation growth of (012) lattice plane. The Ag NPs dispersed in the thin film introduced the percolation behavior into composite the thin film, having the theoretical percolation threshold of f c = 0.131. When the volume fraction of Ag NPs is about 0.12 (Ag/Fe = 0.6). The dielectric constant of the Ag NPs/BiFeO3 thin film reached about 173, being three times as large as that of BiFeO3 thin film without Ag NPs. The minimum value of the dielectric loss was about 0.1–0.2. The typical ferromagnetic property was maintained although the magnetizations decreased a little with the increase in Ag content. The coercive force was 111Oe, showing no typical difference between the thin films with and without Ag NPs. They were beneficial to be used as a candidate in devices with both dielectric and ferromagnetic properties at the same time.

Preparation and Properties of Bi Doped AgSnO2(12) Electrical Contact Materials

Preparation of Cubic Zinc Stannate Nanopowder and Its Application in Silver-Based Electrical Contact Material

Interfacial wettability and electrical properties of Ni-doped Ag/Bi2Sn2O7 electrical contact materials

Controllable Preparation of SnO2 Solid Microsphere and Its Application in Electrical Contact Material

A Novel Method for the Preparation of Ag/SnO 2 Electrical Contact Materials

Research Progress in AgSnO2 Electrical Contact Materials

Phase Structure Analysis of AgCd and AgSn Alloy Powders

Effect of the impurity in electroless plated Powders on morphology and properties of sintered AgSnO2 materials

Electrical Contact Characteristics of Ag-SnO2 Materials with Increased SnO2 Content

Effects of Coating Process on the Characteristics of Ag–SnO2 Contact Materials

Influences of Tin Oxide Surface Modification on the Morphology and Performance of Sintered Ag/SnO2 Composite Powders

Study on Simulation and Experiment of Y-Mo Co-Doped AgSnO2 Contact Materials

Theoretical calculation and experimental study on the conductivity and stability of Bi-doped SnO2 electrode

Electrical Performance of Cu Doped AgSnO<sub>2</sub>In<sub>2</sub>O<sub>3</sub> Electrical Contacts Fabricated by Internal Oxidation

Preparation and Arc Erosion Mechanism of Ni Skeleton Reinforced Ag-Based Contact Materials with CuO-Coated SnO2

Effect of Ag Doping on the Formation and Properties of Percolative Ag/BiFeO 3 Composite Thin Film by Sol–gel Method

Anti-Arc Erosion Properties of Ag-La2Sn2O7/SnO2 Contacts

Preparation and Arcing Characteristics of Ag/SnO2 Electrical Contacts

Influences of Metal Oxide Additions on the Morphology of Sintered AgSnO2 Composite Powders

Investigation of the Microstructure and Electrical Performance of Ag/SnO 2 In 2 O 3 Contacts with Nickel Addition Fabricated by Internal Oxidation

Synthesis and Characterization of Sn1-xBixO2 Nano-powder