Insight into the Action Mechanism of Ammonia in One-Pot Synthesis of Hermetic Al@Ag Core–Shell Particles Via Deposition Model

Congqing Yang,Mingxi Pan,Hui Huang,Jun Guo,Chao Gao,Hu Li,Huaidi Gu

DOI: https://doi.org/10.1016/j.colsurfa.2023.131480

2023-04-19

Abstract:In this study, particles with hermetic silver shell were successfully prepared by a facile one-pot electroless plating method and the effect of NH 3 ·H 2 O in reaction process was investigated. The result shows that the concentration ratio of NH 3 ·H 2 O to Ag + from 18:1 to 55:1 triggers a continuous transition of the silver coating from raspberry-like granule to hermetic and then loose. This transition is mainly dependent on the suppression of Ag deposition as increasing NH 3 ·H 2 O concentration. It was confirmed using silver deposition kinetic and electrochemistry tests. Based on these experimental results, a deposition model was proposed to quantify the specific behavior of NH 3 ·H 2 O in inhibiting Ag deposition from the perspective of interfacial reaction between active center and [Ag(NH 3 ) 2 ] + . The deposition model was fitted well with experimental results and the effective chemical reaction rate ( keff ) at solid-liquid interface were calculated, which is the critical factor affecting nucleation and coating quality. As CNH3·H2O:CAg+ =48:1, keff is 0.0117 mol L -1 min -1 , a compact core-shell particle is realized and the resistivity as low as 1.21×10 -4 Ω·cm even with Ag content is 15.61 wt%. This work revealed the dual role of NH 3 ·H 2 O in complexing Ag + and regulating keff to control silver grain size and distribution.

chemistry, physical