Abstract:In this research, we creatively integrate the traditional methods of liquid precursor infiltration plus in situ precipitation with stereolithography-based 3D printing for the fabrication of Al2O3-ZrO2 ceramics to ensure the homogeneous distribution of ZrO2 particle in the alumina matrix. Our characterization results shows that this combination leads to the materials with significantly better performance. The Al2O3 specimen is soaked in a Zr4+ ion solution to induce infiltration, in-situ precipitation and then sintered. X-ray diffraction analysis of the thus-treated sample indicated that Al2O3 was the primary phase and t-ZrO2 was the secondary phase. Microstructural and EDS analysis showed that the ZrO2 particles were homogeneously distributed in the Al2O3 matrix, leading to inhibited grain growth. The samples soaked in solutions for different Zr4+ concentrations and sintered both at 1450 degrees C and 1550 degrees C showed improved mechanical properties as compared to those of pure alumina. Futhermore, the sample infiltrated using the solution with a concentration of 1.5 mol/L and sintered at 1450 degrees C showed similar fracture toughness (4.97 MPa m(1/2)) with the sample sintered at 1550 degrees C (5.06 MPa m(1/2)) but much better hardness (20.95 Gpa) than the sample sintered at 1550 degrees C (19.71 GPa). Therefore, this method could not only enhance the mechanical properties via introducing the second phase, but also lowers the sintering temperature by at least 100 degrees C, which would be beneficial for energy conservation and leads to significant advances in the 3D printing of ceramic components. (C) 2018 Elsevier B.V. All rights reserved.

Interfacial research on interpenetrating network structure ZrO2/Al-Mg composites prepared by Extrusion Freeform Fabrication 3DP and pressureless infiltration

In situ (Al3Zrp+Al2O3np)/2024Al metal matrix composite with controlled reinforcement architecture fabricated by reaction hot pressing

Fabrication of Nanocrystalline Zro2 Particle Reinforced Aluminum Alloy Composite by Squeeze Casting Route

Novel MMC Microstructures Prepared by Melt Infiltration of Reticulated Ceramic Preforms

High-Resolution Electron Microscope Observation of Interface Microstructure of A Cast Al-Mg-Si-Bi-Pb(6262)/Al2o3p Composite

An Al-Al interpenetrating-phase composite by 3D printing and hot extrusion

Preparation of Al2O3/AZ91D Mg Interpenetrating Composites Using Lost Foam Casting Combined with Layered Extrusion Forming

Fabrication of 3D-SiC/aluminum alloy interpenetrating composites by DIW and pressureless infiltration

In situ infiltration behavior and interfacial microstructure evolution between Al and carbon fibers

Effects of interfacial diffusion induced infiltration process on the microstructure evolution and interfacial enhancement of CF/Mg composites

Dispersion and Preparation of Nano-AlN/AA6061 Composites by Pressure Infiltration Method

Fabrication of High-Performance Al2O3-ZrO2 Composite by a Novel Approach That Integrates Stereolithography-Based 3D Printing and Liquid Precursor Infiltration

A ZA22/Al interpenetrating phase composite with high compressive stress plateau and high damping capacity

Simulation and Experimental of Infiltration and Solidification Process for Al2O3(3D)/5083Al Interpenetrating Phase Composite for High Speed Train Prepared by Low-Pressure Infiltration

The effect of interface reaction on the thermal and mechanical properties of Mn3.2Zn0.5Sn0.3N/Al composites

Interfacial microstructure and strengthening mechanisms of Cf/Mg composite with double-layer interface

Microstructure and mechanical behavior of Mg ZK60/Al 1100 composite plates fabricated by co-extrusion

Microstructures and enhanced mechanical properties of (Al3Ti+Al2O3)/Al–Si composites with co-continuous network structure prepared by pressure infiltration

Mg/ZrO2 Metal Matrix Nanocomposites Fabricated by Friction Stir Processing: Microstructure, Mechanical Properties, and Corrosion Behavior

Co-continuous Al/Al2O3 composite produced by liquid displacement reaction: Relationship between microstructure and mechanical behavior

Microstructure of Diamond/aluminum Composites Fabricated by Pressureless Metal Infiltration