Phase equilibria of the Nb–Si-Gd ternary system at 1273 K

Xiaoxi Xu,Baiyang Pan,Jie Yang,Qianxin Long,Lichun Cheng,Qingrong Yao,Zhao Lu,Jianqiu Deng

DOI: https://doi.org/10.1016/j.mtcomm.2024.109119

IF: 3.8

2024-05-06

Materials Today Communications

Abstract:The phase equilibria of the Nb–Si-Gd ternary system at 1273 K in all the composition ranges were investigated by X-ray diffraction (XRD), electron probe microanalysis (EPMA), and Scanning electron microscopy (SEM) equipped with Energy dispersive spectroscopy (EDS). The isothermal section comprises 12 single-phase regions, 22 two-phase regions, and 11 three-phase regions. The existing of Nb 3 Si phase was confirmed at 1273 K by couple diffusion. A new ternary compound Gd 2 Nb 3 Si 4 was discovered and its crystal structure was analyzed by the Rietveld method with Rwp = 2.11%, Rp = 1.54%, R exp = 0.75%. It belongs to the space group P4 1 2 1 2 (No.92) with the lattice parameter a = b = 6.99048 Å, c = 12.94393 Å, α = β = γ = 90°.