Effects of structural transformation on magnetic properties of AlCoFeCr high-entropy soft magnetic powder cores by adjusting Co/Fe ratio

Wei Gao,Yaqiang Dong,Yan Ma,Xingjie Jia,Zhonghao Liu,Xubin Li,Ronglin Zhao,Shouding Wu,Qiang Li,Aina He,Jiawei Li,Hang wu

DOI: https://doi.org/10.1016/j.matdes.2022.111537

2022-12-25

Abstract:Al 1.5 (Co x Fe 6-x ) 6 Cr high-entropy alloy (HEA) soft magnetic powder cores (SMPCs) were designed and prepared via gas atomization and insulation, and the effects of the Co/Fe ratio on their phase formation, microstructure evolution, and soft magnetic properties were systematically investigated. An increase in Co content promoted the precipitation of the B2 phase from the body-centered cubic (BCC) matrix, and the content of the B2 phase was greater than that of the BCC phase at x = 4, thus replacing the BCC phase as the matrix, which contributed to the optimization of the soft magnetic properties of the AlCoFeCr HEA. The SMPC composed of the BCC single phase exhibits the lowest eddy current loss ( P e ) of 55.1 mW/cm 3 (@100 kHz, 50 mT), excellent direct current (DC) bias performance of 80.6% at 100 Oe, and high stable effective permeability ( μ e ) of 49.9 up to 1 MHz. The association of magnetic domains, grain size, and particle size with H c variation was analyzed, providing guidelines for subsequent studies to obtain HEAs with good soft magnetic properties. By comprehensively and systematically comparing the microstructural differences of diverse matrix-phase HEAs and SMPCs, the specific application of this HEA system under high-temperature conditions can be expanded.

materials science, multidisciplinary

What problem does this paper attempt to address?

This paper aims to solve the optimization problem of high - entropy alloys (HEAs) in soft magnetic properties, especially to study the influence of adjusting the Co/Fe ratio on the phase formation, microstructure evolution and soft magnetic properties of AlCoFeCr high - entropy alloy soft magnetic powder cores. Specifically, the paper focuses on the following aspects:

1. **Phase Formation and Microstructure Evolution**:
- The influence of different Co/Fe ratios on the phase formation and microstructure evolution of Al1.5(Co xFe6 - x)6Cr high - entropy alloy soft magnetic powder cores was studied.
- It was found that with the increase of Co content, the precipitation of B2 phase from the body - centered cubic (BCC) matrix was promoted, and when x = 4, the content of B2 phase exceeded that of BCC phase and replaced BCC phase to become the matrix.

2. **Soft Magnetic Property Optimization**:
- By adjusting the Co/Fe ratio, the soft magnetic properties of AlCoFeCr high - entropy alloy were optimized.
- The research found that the soft magnetic powder core composed of single - phase BCC showed the lowest eddy - current loss (\( P_e \)), and had good DC bias performance and stable effective permeability.

3. **Relationship between Magnetic Domains, Grain Size, Particle Size and Coercivity (\( H_c \))**:
- The relationship between magnetic domains, grain size, particle size and the change of coercivity (\( H_c \)) was analyzed, which provided guidance for subsequent research.

4. **Application Prospects**:
- By systematically comparing the microstructure differences between HEAs with different matrix phases and soft magnetic powder cores, the application prospects of this HEA system under high - temperature conditions were expanded.

Through experimental and computational methods, the paper discussed in detail the influence of Co/Fe ratio on the phase formation, microstructure and soft magnetic properties of Al1.5(Co xFe6 - x)6Cr high - entropy alloy soft magnetic powder cores, providing theoretical basis and technical support for the development of high - entropy alloy materials with excellent soft magnetic properties.