Abstract:A series of BaSr2Sc4O9 and Ce3+-doped BaSr2Sc4O9 phosphors were synthesized via the high temperature solid state reaction. Crystal structure information on BaSr2Sc4O9 is first refined using the Rietveld method based on the XRD data, and it is assigned to the trigonal system with the R3 space-group. The photoluminescence properties were investigated in detail, including the emission and excitation spectra, site occupation, decay lifetime, thermal quenching, and quantum efficiency. There are three Ba2+/Sr2+ sites and four Sc3+ sites in this structure. The Ce3+ ions in the 6-fold coordinated Sr2+/Ba2+ sites show a near-ultraviolet-blue emission with a peak at around 407 nm under ultraviolet excitation. The Ce3+ ions in Sc3+ sites exhibit a bright broad orange-red emission with the peak at around 615 nm under near-ultraviolet and blue excitation. The energy transfer process between the different sites is demonstrated based on the spectral analysis, theoretical calculation, and decay lifetime variation. Under excitation of 345 nm, the energy transfer phenomenon and distribution of activator ions lead to the invalidation of part of the Ce3+ ions, and then it causes a higher concentration quenching point. The participation of the energy transfer in the thermal quenching phenomenon causes the abnormal intensity variation, which is ascribed to the energy compensation by the increasing energy transfer efficiency at high temperature. The internal quantum efficiency is 45% under the 420 nm excitation wavelength. An excellent white light emitting diode lamp is obtained by fabricating BaSr2Sc4O9:Ce3+ with BAM:Eu2+, β-sialon:Eu2+, and a 395 nm GaN chip; its CIE coordinate ( x, y), CCT, and Ra are (0.3708, 3463), 4023 K, and 84. These results reveal the correlation between energy transfer and luminescent property and provide a practical foundation to comprehend and adjust the photoluminescence performance.

Ce concentration dependence on scintillation properties of SrHfO3 single crystals

Growth and Scintillation Properties of Cs2LiLa0·1Y0·9Cl6:Ce Crystal

Temperature dependence and quenching characteristics of (La, Gd)$_2$Si$_2$O$_7$ scintillators at various Ce concentrations

Multiemission of Ce 3+ from a Single Crystallographic Site Induced by Disordering of Ions

Preparation and Photoluminescence Properties of Fluorosilicate Glass Ceramics Containing Ceof: Dy3+ Nanocrystals

Scintillation properties of transparent Lu‐α‐SiAlON:Ce3+ ceramics

A Cerium Doped Scandate Broad Orange-Red Emission Phosphor and its Energy Transfer-Dependent Concentration and Thermal Quenching Character

Preparation and Luminescence Properties of Ce3+/Dy3+-codoped Fluorosilicate Glass Ceramics

Effect of Microstructure on the Radioluminescence and Transparency of Ce-Doped Strontium Hafnate Ceramics

Crystal growth and optical properties of Ce-doped (La,Y)$_2$Si$_2$O$_7$ single crystal

Preparation and luminescence properties of Ce3+ and Tb 3+ co-doped glasses and glass ceramics containing SrF2 nanocrystals

Scintillation properties of non-doped and Ce-doped LiAl5O8 single crystals

Efficient energy transfer of Ce to Nd in SrF2 transparent ceramics for enhancing NIR emission

Characteristics of Ce-doped phosphate inorganic glass scintillators for gamma- and X-ray detection

Physical and luminescence properties of Ce 3+ activated strontium phosphate glasses

Ce3+, Pr3+ Co-Doped Lu3Al5O12 Single Crystals and Ceramics: A Comparative Study

High Efficiency Medical Scintillator Lu2sio5 : Ce Studied by Vuv Spectra

Crystal Growth, Photoluminescence and Radioluminescence Properties of Ce3+-Doped Ba3Y(PO4)3 Crystal

Solution Synthesis and Light-Emitting Applications of One-Dimensional Lead-Free Cerium(III) Metal Halides

Influence of Activator Concentration on the Spectral-Luminescence and Scintillation Properties of YAG:Ce Crystals

Photoluminescence and Thermoluminescence of Ce3+ Incorporated Y3Al5O12 Synthesized by Rapid Combustion