Crystal Growth, Photoluminescence and Radioluminescence Properties of Ce3+-Doped Ba3Y(PO4)3 Crystal

Zhenggang Zou,Jiaolin Weng,Chun Liu,Yiyang Lin,Jiawei Zhu,Yijian Sun,Jianhui Huang,Guoliang Gong,Herui Wen

DOI: https://doi.org/10.3390/cryst14050431

IF: 2.7

2024-05-01

Crystals

Abstract:Inorganic scintillation crystals have been widely used in applications of high-energy physics, nuclear medical imaging, industrial nondestructive inspection, etc. In this work, a single crystal Ba3Y(PO4)3 (BYP) with 1.0 at% Ce3+-doping concentration was first grown by the Czochralski method, and the electronic structure was calculated using first principles based on density functional theory. In addition, a series of Ce3+-doped BYP phosphors were synthesized, and the fluorescence emission under UV excitation was measured through low-temperature spectroscopy, containing double-peaked emission from 5d–4f transition and self-trapped exciton recombination. A comparison of the UV and X-ray-excited fluorescence spectra reveals the existence of oxygen vacancies as well as F+ centers in the crystal. The air annealing of the crystal effectively reduces the thermoluminescence defects but reduces the emission intensity under UV or X-ray excitation. The BYP:Ce crystal shows a fast decay lifetime of 15.5 ns, and the fast component is as short as 8 ns. The results show that the Ce3+-doped BYP crystal has potential as a kind of scintillator with fast decay properties.

materials science, multidisciplinary,crystallography