Efficient energy transfer of Ce to Nd in SrF2 transparent ceramics for enhancing NIR emission

Yongqiang Zhang,Zhiwei Zhou,Bingchu Mei

DOI: https://doi.org/10.1016/j.jeurceramsoc.2023.07.038

IF: 5.7

2023-07-01

Journal of the European Ceramic Society

Abstract:High optical quality Nd3+ and Ce3+ co-doped SrF2 (Nd3+, Ce3+: SrF2) transparent ceramics were fabricated successfully by a simple hot-pressing (HP) method. The phase composition, in-line transmittance, absorption and emission spectra, as well as the detailed energy transfer of Nd3+ and Ce3+ were investigated. In addition, the Judd- Ofelt (J-O) theory was adopted to evaluate the luminescence property. The SrF2 transparent ceramic samples exhibited excellent optical properties, up to 82 % at 400 nm and 92.5 % at 1054 nm. The fracture surface of SrF2 transparent ceramic proved nearly dense microstructure and EDS results demonstrated uniform doping. The addition of cerium ions changed the crystal field environment of neodymium ions and shifted the emission peak to higher wavelengths at 796 nm excitation. Moreover, through the energy transfer process of Ce3+ to Nd3+, the occurrence of concentration quenching phenomenon was avoided under 298 nm excitation, and the emission cross-section of 4F3/2→4I11/2 increased to 3.1 × 10−20 cm2.

materials science, ceramics