Abstract:Core-shell structured SiC/SiO2 nanowires (SiC/SiO2 NWs) were synthesized by a simple thermal evaporation method without a catalyst. The influence of the growth temperature and holding time on the microstructure and composition of the nanowires were investigated. The results indicate that within the temperature range of 1150 to 1550 degrees C, the color of SiC/SiO2 nanowires gradually transitions from pure white to off-white with increasing temperature. During this process, the average diameter of SiC/SiO2 increases from 74 nm to 291 nm, while the surface SiO2 layer thickness decreases from 17 nm to 5 nm, with nanowires can reach lengths of hundreds of micrometres. Variations in supersaturation of SiO and CO at different temperatures lead to discrepancies in nanowire diameter and SiO2 shell thickness. At 1350 degrees C, prolonged holding time enhances silicon powder reaction, resulting in increased structural disorder of the obtained SiC/SiO2 nanowires. The nanowire growth follows a vapor-solid (V-S) mechanism. Additionally, the study demonstrates that the photoluminescence (PL) characteristics of the nanowires exhibit a blue shift attributable to their nanoscale dimensions, while variations in emission spectra correlate with stacking faults, SiC diameter, and SiO2 thickness. This work may be provide a theoretical basis for preparing SiC/SiO2 nanowires with different diameters and SiO2 shell thicknesses, which is crucial for advancing the development and application of SiC/SiO2 nanoceramics.

Green synthesis of blue-green photoluminescent β-SiC nanowires with core-shell structure using coconut shell as carbon source

Syntheses and photoluminescence properties of SiC nanowires with different colors

Catalytic Synthesis and Growth Mechanism of SiC@SiO2 Nanowires and Their Photoluminescence Properties

Silicon Nanowire Synthesis by Chemical Vapor Deposition

In-situ Synthesis of SiC/SiO2 Nanowires by Catalyst-Free Thermal Evaporation of Silicon Powder and Their Photoluminescence Properties

Synthesis of SiC/SiO2 core–shell nanowires with good optical properties on Ni/SiO2/Si substrate via ferrocene pyrolysis at low temperature

Core‐shell SiC/SiO2 Heterostructures in Nanowires

Preparation of 2H/3C–SiC heterojunction nanowires from molten salt method with blue shift photoluminescence property

Synthesis of large-scale SiC@SiO2 nanowires with good optical properties by using Si@SiO2 as silicon source

Catalyst-assisted Synthesis of Core–shell SiC/SiO 2 Nanowires Via a Simple Method

Highly Efficient and Stable Photoluminescence from Silicon Nanowires Coated with Sic

Synthesis of Β-Sic Nanowires Via a Facile CVD Method and Their Photoluminescence Properties

Large-scale synthesis and photoluminescence properties of SiC/SiOx nanocables

Synthesis and Characterization of Ultralong SiC Nanowires with Unique Optical Properties, Excellent Thermal Stability and Flexible Nanomechanical Properties

Self-Seeded MOCVD Growth and Dramatically Enhanced Photoluminescence of InGaAs/InP Core–Shell Nanowires

Tunable Violet–blue Emission from 3C-Sic Nanowires

Synthesis and characterization of multiwalled carbon nanotube/CdS core/shell heterostructures

Silica-coated and annealed CdS nanowires with enhanced photoluminescence

Spatial bandgap engineering along single alloy nanowires.

High-Yield Synthesis of SiC@SiO2 Core-Shell Nanowires on Graphite Substrates for Energy Applications

Synthesis of SiO2 covered SiC nanowires with milled Si,C nanopowders