Corrosion Resistance of Tungsten-Carbide-Rich Coating Layers Produced by Noble Gas Ion Mixing

A.S. Racz,Z. Kerner,Miklos Menyhard

DOI: https://doi.org/10.2139/ssrn.4155113

2022-01-01

SSRN Electronic Journal

Abstract:Tungsten-carbide (WC)-rich layers have been produced by irradiating C/W multilayers with noble gases at room temperature. The in-depth distribution of the elements and compounds before and after the ion irradiation has been measured by Auger electron spectroscopy depth profiling. The growth of the WC-rich layer started at the interfaces and with increasing fluence the separately growing layers coalesced. The in-depth distribution of the formed carbide could be tailored by varying the applied projectiles, fluences energies and initial layer structure. The corrosion resistance of the formed layers has been tested in 3.5 wt% NaCl solution. For finding connection between the carbide distribution and corrosion resistance the term effective areal density has been introduced showing the jump in the corrosion resistance. If effective areal densities were lower and higher than 550 (1/nm 2 ) and 1200 (1/nm 2 ), resp., the corrosion current densities were 0.5 and 0.08 (µA/cm 2 ). The maximum corrosion resistance found was better than that of stainless steel and WC cermet. The effective areal density of WC carbide produced and thus the corrosion resistance could be predicted by TRIDYN simulations allowing the design of corrosion resistive layers by fast and cheap simulation method.