Abstract:The substrate of as-cast Ni-28 wt% Sn hypoeutectic alloy immersed in liquid nitrogen is rapidly remolten and solidified by laser surface remelting with a scanning velocity of 10 mm/s and the laser power of 1950 W. The microstructure of the substrate and its effect on the microstructure of the molten pool are investigated by scanning electron microscope carefully. It is found that the substrate of the Ni-28 wt%Sn ingot is composed of coarse primary α-Ni dendrites and the interdendritic (α-Ni+Ni3Sn) eutectic. The growth orientations of α-Ni dendrites and the interdendritic eutectic are distributed nearly randomly in the as-cast substrate. There are three kinds of microstructure characterstic zones from the top to the bottom of melted pool. The growth directions of α-Ni dendrites with the primary dendritic spacings ranging from 4.19 to 6.91 μm are approximately parallel to the laser scanning direction at the top of the molten pool due to the fact that the temperature gradient at the interface between the molten pool and substrate tends to be parallel to the laser scanning direction. In the middle of the molten pool, the epitaxial α-Ni columnar dendrites are found to be inclined to grow in the direction vertical to the bottom of the molten pool due to the fact that the temperature gradients in most zones of the molten pool are perpendicular to the bottom of the molten pool. The formation of new primary dendrites by the growth of the tertiary arm results in the decrease of primary dendritic spacing in comparison with that at the bottom of the molten pool. There are a small quantity of residual α-Ni primary phase and a large amount of (α-Ni+Ni3Sn) eutectic at the bottom of the molten pool. The microstructure of laser remolten zone is greatly influenced by the substrate microstructure, and the growth direction of the α-Ni dendrite in the molten pool is also affected remarkably by both the heat flux and the preferred crystal orientations for dendritic growth. Compared with the mixed lamella, rod and divorced (α-Ni+Ni3Sn) eutectic microstructures in the substrate, the eutectic structure in the molten pool is completely composed of the refined lamellar eutectic, which grows epitaxially in the direction perpendicular to the interface between the molten pool and the substrate at the bottom of molten pool. The eutectic lamellar spacing increases from the top (0.23 μm± 0.01 μm) to the bottom (0.42 μm± 0.02 μm) of the molten pool due to the interface growth velocity decreasing from the top to the bottom. The Kurz-Giovanola-Trivedi model for rapid dendritic growth and the Trivedi-Magnin-Kurz model for eutectic growth are used to estimate the growth undercooling of the microstructure in the molten pool respectively. It is found that the growth undercooling of dendrites and the eutectic in the molten pool should be between 50.4 K and 112.5 K, which is much larger than the critical undercooling for anomalous eutectic growth found in the high undercooled solidification in the previous researches. This phenomenon means that the critical undercooling for anomalous eutectic growth reported in the previous literature may be not the sufficient condition for generating the anomalous eutectic.

Laser remelting of AlSi10Mg(-Ni) alloy surfaces: influence of Ni content and cooling rate on the microstructure

Microstructure and Wear Resistance of Laser-Treated and Slow Cooled AlSi10Mg-(x)Ni Alloys

Influence of Mg Content on Microstructure Coarsening, Molten Pool Size, and Hardness of Laser Remelted Al(- x)-Mg-Sc Alloys

Microstructure and character of laser remelting of plasma sprayed coating (Ni-Cr-B-Si) on Al-Si alloy

Influences of Laser Remelting Treatments on Microstructure and Tensile Properties of Multiphase Ni3Al-based Intermetallic Alloy

Microstructure and Oxidation Resistance of Laser Remelted Nb-18Ti-14Si-9Al Alloy

Influence of Ni Contents on Microstructure and Mechanical Performance of AlSi10Mg Alloy by Selective Laser Melting

Microstructural Evolution of Laser Surface Remelting Ni-28 Wt% Sn Alloy under Liquid Nitrogen Cooling

Nonequilibrium Synthesis of Ni-Al-Si Alloys by Laser Processing

Effect of Cooling Rates on As-Cast Microstructures of Mg-9Al-xSi (x=1, 3) Alloys

Effect of Solidification Conditions on Microstructure and Mechanical Properties of γ-Ni/Mo2Ni3Si Alloy

Phase Selection and Microstructural Formation of Rapidly Directionally Solidified Peritectic Fe–Ni Alloys by Laser Surface Remelting

Evaluation of Microstructure and Hardness of Novel Al-Fe-Ni Alloys with High Thermal Stability for Laser Additive Manufacturing

Microstructure And Mechanical Property Of Alsi10mg Alloy Prepared By Laser Solid Forming

Solidification of Niobium-Silicide-based Alloys During Laser Additive Manufacturing Process

Effect of Laser Remelting on Tribological Performance of Ni-Cr-B-Si Coatings Deposited by Laser Metal Deposition

Study on Laser Surface Remelting of Plasma-Sprayed Al–Si/1wt% Nano-Si3n4 Coating on AZ31B Magnesium Alloy

Laser surface melting of Al-12Si-4Cu-1.2Mn alloy

Laser deposition of refractory MO- NI alloys

Microstructure Evolution in Laser Surface Remelting of Ni–33wt.%Sn Alloy

Intermetallic compound formation during laser alloying of aluminum alloys with metals