Abstract:Modifying bismaleimide (BMI) resin to improve its toughness and flame retardancy without sacrificing the glass transition temperature (Tg) and thermal decomposition stability is still a challenge. In this study, we employed the allyl ether of resveratrol (AER) and eugenol allyl ether grafted polysiloxane (PMES‐Allyl) to co‐modify BMI resin. For the BMI/AER/PMES‐Allyl (BAPA) resin, the content of PMES‐Allyl was 15 wt%, and the molar ratio of maleimide and allyl groups was controlled as 1:0.8. Compared to commercial 2,2′‐diallyl bisphenol A modified BMI (BD) resin, the BAPA resin exhibited superior thermal properties after curing, due to the role of AER in improving the crosslinking density and chain rigidity of the network. The cured BAPA resin had a Tg more than 380°C, and its initial thermal decomposition temperature (Td5%) and char yield (Y800°C) reached 424.8°C and 46.4%, respectively. Meanwhile, PMES‐Allyl as a rubber phase could effectively improve the toughness of the cured resin. The impact strength of the cured BAPA resin was 15.2 kJ/m2. Moreover, the two modifiers both helped to improve the flame retardancy of the material. Compared with the cured BD resin, the cured BAPA resin showed a decrease of peak heat release rate (PHRR), total heat release (THR), and maximum average rate of heat emission (MARHE) by 25.5%, 35.5%, and 31.5%, respectively. Its total smoke production (TSP) was only 35.6% of that of the cured BD resin. In addition, the cured BAPA resin also displayed a lowered water absorption and improved thermal aging resistance. Therefore, it is suggested to be a promising and high‐performance thermosetting resin for cutting‐edge applications.

Toughened of bismaleimide resin with improved thermal properties using amino-terminated Poly(phthalazinone ether nitrile sulfone)s

Enhanced toughness and thermal properties of bismaleimide resin based on the synergistic effect of reactive amino‐terminal poly(phthalazinone ether nitrile sulfone) and bisallyl bearing diphenol group

Morphology and mechanical properties of poly(ether-imide)-modified polycyanurates

Preparation of PBT/POE‐g‐GMA/PP Ternary Blends with Good Rigidity–toughness Balance by Core–shell Particles

Preparation and properties of bismaleimide resin blended with alkynyl-terminated modifiers

High‐performance thermoplastic toughener for bismaleimide resin: Feature application of reactive polyarylether ketone bearing propenyl group

Characterization and properties of high-temperature resistant structure adhesive based on novel toughened bismaleimide resins

Optimization and preparation of an allyl phenoxy-modified bismaleimide resin

Relationship between structure and properties in high-performance PA6/SEBS-g-MA/(PPO/PS) blends: The role of PPO and PS

Toughening and strengthening of low-temperature resistant epoxy resins by introducing high-performance thermoplastic resin with phthalazinone structure

Curing kinetics, thermal and erosive wear characteristics of bismaleimide blends modified by polyaryletherketone

Studies of modified bismaleimide resins Part I The influence of resin composition on thermal and impact properties

Nitrogen-Rich Perylene Nanosheet Enhanced Bismaleimide Resin

Thermal Stability of Allyl-Functional Phthalonitriles-Containing Benzoxazine/Bismaleimide Copolymers and Their Improved Mechanical Properties

Mechanical and thermal properties of a novel bismaleimide matrix resin for high-performance composite materials

A New Strategy to Improve the Toughness of Epoxy Thermosets—By Introducing Poly(ether nitrile ketone)s Containing Phthalazinone Structures

Polyetherimide-modified bismaleimide resins. II. Effect of polyetherimide content

POLYESTERIMIDE-MODIFIED BISMALEIMIDE RESINS. I. EFFECT OF POLYESTERIMI DE CONTENT

Improved mechanical properties of basalt fiber/phthalonitrile composites modified by thermoplastic Poly(phthalazinone ether nitrile)s

On Polyetherimide Modified Bismaleimide Resins, 1 Effect of the Chemical Backbone of Polyetherimide

Bismaleimide resin co‐modified by allyl ether of resveratrol and allyl ether of eugenol‐grafted polysiloxane with enhanced toughness, heat resistance, and flame retardancy