Abstract:In this study, the mechanical, microstructural, and crystallographic effects of ball-burnishing applied to Al 7075-T6 alloy at 0.15–0.30 mm penetration depth, 0.15–0.30–0.60 mm/rev changing feed rates and 100–200 rpm range were investigated. After the ball-burnishing processes were carried out in different parameters, surface roughness measurements were applied to determine the surface qualities, and hardness and impact energy tests were applied to characterise the mechanical properties. Dislocation density and texture coefficient values were calculated by determining the crystallographic properties using X-ray diffraction. It has been determined that the ball-burnishing process directly affects the surface roughness, depending on the increasing rotational speed and feed rate. As a result of microstructural investigations, the average grain size decreased with increasing amount of deformation on the sample surface. At 200 rpm ball-burnishing parameter, the surface hardness of the sample increased by approximately 41% compared to the initial state and was measured as 265 HV2. It was determined that the ball-burnishing process did not positively affect the impact of the toughness of the alloy. The reason for this is that the roughness and scratches on the surface caused by the ball-burnishing process have a notch effect, increasing the crack formation and propagation speed. Dans cette étude, on a investigué les effets mécaniques, microstructuraux et cristallographiques du brunissage à bille appliqué à l'alliage Al 7075-T6 à une profondeur de pénétration de 0.15-0.30 mm, un changement de vitesses d'alimentation de 0.15-0.30-0.60 mm/tour et une plage de 100 à 200 tr/min. Après complétion des procédés de brunissage à bille selon les différents paramètres, on a effectué des mesures de rugosité de surface pour déterminer les qualités de surface, et l'on a effectué des essais de dureté et d'énergie de frappement pour caractériser les propriétés mécaniques. On a calculé les valeurs de densité des dislocations et de coefficient de texture en déterminant les propriétés cristallographiques à l'aide de la diffraction des rayons X. Il a été déterminé que le procédé de brunissage à bille affectait directement la rugosité de la surface, en fonction de l'augmentation de la vitesse rotationnelle et de la vitesse d'alimentation. À la suite des examens microstructuraux, la taille moyenne des grains diminuait avec l'augmentation de la quantité de déformation sur la surface de l'échantillon. Au paramètre de brunissage à bille de 200 tr/min, la dureté de surface de l'échantillon augmentait d'environ 41% par rapport à l'état initial et était mesuré à 265 HV2. Il a été déterminé que le procédé de brunissage à bille n'avait pas d'effet positif sur la ténacité de l'alliage. La raison en est que la rugosité et les égratignures sur la surface résultant du procédé de brunissage à bille ont un effet d'entaille, augmentant la formation de fissures et leur vitesse de propagation.

Investigation of the Effects of Slide Diamond Burnishing Process on the Mechanical Performance of GCr15 Steel

Multi-objective optimization of slide diamond burnishing parameters for enhanced fatigue resistance of AISI 52100 steel

The Influence of Slide Burnishing on the Technological Quality of X2CrNiMo17-12-2 Steel

Improving surface integrity by optimizing slide diamond burnishing parameters after hard turning of 42CrMo4 steel

Effect of Roller Burnishing and Slide Roller Burnishing on Fatigue Strength of AISI 304 Steel: Comparative Analysis

Surface Hardness Modification of Selective Laser Melted Ti6Al4V Parts by Sliding Friction Diamond Burnishing

Characterization of Surface Integrity of 3D-Printed Stainless Steel by Successive Grinding and Varied Burnishing Parameters

Effect of Roller Burnishing and Slide Roller Burnishing on Surface Integrity of AISI 316 Steel: Theoretical and Experimental Comparative Analysis

Investigation of the effect of ball-burnishing treatment applied to Al 7075-T6 alloy on mechanical and crystallographic properties

Effect of Diamond Burnishing on Fatigue Behaviour of AISI 304 Chromium-Nickel Austenitic Stainless Steel

Effects of the surface layer of steel samples after ball burnishing on friction and wear in dry reciprocating sliding

Effects of ball burnishing on surface properties of SKD11 mold steel

Surface integrity and fatigue behavior of AISI 4340 steel after hybrid laser-ultrasonic assisted ball burnishing process

Sliding Friction and Wear Properties of GCr15 Steel under Different Lubrication Conditions

Surface Roughness Improvement by Sliding Friction Burnishing of Parts Produced by Selective Laser Melting of Ti6Al4V Titanium Alloy

Shape Accuracy Improvement in Selective Laser-Melted Ti6Al4V Cylindrical Parts by Sliding Friction Diamond Burnishing

Tribological behavior of heat treated AISI 6150 steel

Experimental testing of GCr15 bearing steel with different surface treatments as passive friction energy-dissipative shims

Study on the effect of the strengthen grinding process surface coverage on the micro-morphology, micro-hardness, roughness, and residue stress of GCr15 bearing steels

Multi-roller Taper Burnishing of Internal Chamfers and Its Enhancement Mechanism on 7050 Aluminum Alloy

Effect of ball burnishing process on surface roughness and corrosion behavior of S235JR steel