Abstract:The hot compression tests of Fe-28Mn-11Al-1.5C-5Cr (wt.%) lightweight steel were carried out by Gleeble-3500 at temperature of 900, 1050 and 1150 degrees C with strain rates of 0.01 and 1 s-1. The effect of various precipitates on the hot deformation mechanism and dynamic recrystallization (DRX) mechanism was studied by electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). When deformed at 900 degrees C, the dislocations tend to cut through intragranular ic carbides to form unidirectional microbands and deformation twins. The intergranular precipitates (intergranular ic carbides, B2 (FeAl type) precipitates and (Cr,Mn)23C6 precipitates) hinder the migration of the original grain boundaries, so that the discontinuous DRX (DDRX) is suppressed at the initial stage, but with the increase of strain, the dislocations accumulate at the grain boundaries to promote the nucleation of DRX grains. Meanwhile, the nucleation of DRX grains by continuous DRX (CDRX) mechanism within grains is also activated. Therefore, bimodal distribution of DRX grains is formed at low strain rate of 0.01 s-1, while the degree of DRX is low at high strain rate of 1 s-1. When the deformation temperature is 1050 degrees C, the content of microbands and deformation twins decreases. There are only a few B2 precipitates at the grain boundaries, so the original grain boundaries tend to bulge to promote DDRX nucleation. When deformed at 1150 degrees C, largesized ic carbides are easily formed near the dislocations due to the fast diffusion rate of atoms, which inhibits the formation of microbands and deformation twins, and only slip bands are observed. There is no precipitate on the grain boundary, and the DDRX is the dominant mechanism of DRX. Moreover, the special yield-point-like elongation phenomenon has been proved to be caused by intragranular ic carbides. (c) 2023 The Authors. Published by Elsevier B.V. This is an open access article under the CC

Effect of withdrawal rate on precipitation characteristics of MC-type carbides in a nickel-based directionally solidified superalloy with high Re content

Effect of Solidification Rate on Mc-Type Carbide Morphology in Single Crystal Ni-Base Superalloy Am3

B22-P-17Evolution of the MC Carbide in Nickel-base Single Crystal Superalloy Exposing at 950 °C

Effect of solidification parameters on the microstructures of a single crystal Ni-based superalloy AM3

Influence of Withdrawal Rate on Last Stage Solidification Path of a Mo-rich Ni3Al Based Single Crystal Superalloy

Site Preference of Metallic Elements in M23C6 Carbide in a Ni-based Single Crystal Superalloy

Effect of Directional Solidification Methods on Solid Solution Window in Ni-based Single-Crystal Superalloy

Solidification characteristics and high temperature tensile properties of Ni-based superalloy IN713C

Effect of Withdrawal Rate on Microstructure and Mechanical Properties of a Directionally Solidified NiAl-based Hypoeutectic Alloy Doped with Trace Hf and Ho

Influence of Withdrawal Rate on the Porosity in a Third-Generation Ni-based Single Crystal Superalloy

Grain boundary precipitation behavior in Re-containing nickel-based directionally solidified superalloys with carbon and boron additions

The effect of rhenium on the microstructure stability and γ/γ′ interfacial characteristics of Ni-based single crystal superalloys during long-term aging

Microstructure and Microsegregation in A Ni-Based Single Crystal Superalloy Directionally Solidified under High Thermal Gradient

Effect of cooling rate on carbides in directionally solidified nickel-based single crystal superalloy: X-ray tomography and U-net CNN quantification

Effects of Re and Ru on the Solidification Characteristics of Nickel-Base Single-Crystal Superalloys

Effects of rhenium and high-angle grain boundaries upon the elemental distribution and microstructure of Ni-based single-crystal superalloys

Thermodynamic Simulation Calculation on Precipitation Behavior of Equilibrium Phases in a Low Re bearing Nickel based Single Crystal Superalloy

On the effect of Re addition on microstructural evolution of a CoNi-based superalloy

Numerical Simulation of Temperature Field and Grain Texture During Casting Single Crystal Superalloy DD403 with Liquid Metal Cooling

Unveiling the Re effect on long-term coarsening behaviors of γ′ precipitates in Ni-based single crystal superalloys

Effect of Intragranular Κ Carbides and Intergranular Precipitates on the Hot Deformation Mechanism and Dynamic Recrystallization Mechanism of Fe–28Mn–11Al–1.5C–5Cr Lightweight Steel