A Bithiazole‐Substituted Donor for High‐Efficiency Thick Ternary Organic Solar Cells via Regulation of Crystallinity and Miscibility
Wentao Zou,Chenyang Han,Xu Zhang,Jiawei Qiao,Jifa Yu,Huajun Xu,Huanhuan Gao,Yanna Sun,Yuanyuan Kan,Xiaotao Hao,Guanghao Lu,Yingguo Yang,Ke Gao
DOI: https://doi.org/10.1002/aenm.202300784
IF: 27.8
2023-05-03
Advanced Energy Materials
Abstract:Herein, a bithiazole‐substituted small molecule donor (ZW1) with high crystallinity is synthesized and employed to fabricate ternary devices. The addition of ZW1 enhances the crystallinity of the blend films. Furthermore, the good miscibility between D18 and ZW1 drives Y6 to separate from its mixed phase with D18, optimizing the phase separation and vertical distribution of the active layer. Combining the regulation of crystallinity and miscibility, charge transport and recombination are improved in ternary devices. As a result, outstanding power conversion efficiencies (PCEs) of 18.50% and 16.67% are achieved for 120 nm‐thick and 300 nm‐thick ternary organic solar cells (OSCs), respectively. The 16.67% PCE is one of the highest values for thick‐film OSCs reported to date. Organic solar cells (OSCs) with thick active layers exhibit great potential for future roll‐to‐roll mass production. However, increasing the thickness of the active layer generally leads to unfavorable morphology, which decreases the device's performance. Therefore, it is a critical challenge to achieve OSCs with high efficiency and thick film simultaneously. Herein, a small molecular donor, ZW1, incorporating a bithiazole unit along with a thiophene group as a π‐bridge is reported. ZW1 with high crystallinity is employed to fabricate D18:ZW1:Y6 ternary devices, which enhances the crystallization, optimizes the morphology, and suppresses bimolecular recombination. Additionally, ZW1 shows better miscibility with D18, resulting in the preferred vertical phase distribution. As a result, an outstanding power conversion efficiency (PCE) of 18.50% is realized in ternary OSCs with 120 nm active layer thickness. Importantly, the thick ternary OSCs attain a high PCE of 16.67% (thickness ≈300 nm), significantly higher than the corresponding binary devices (13.50%). The PCE of 16.67% is one of the highest values for thick‐film OSCs reported to date. This work demonstrates that the incorporation of highly crystalline small‐molecule donors into ternary OSCs, possessing good miscibility with host materials, presents an effective strategy for fabricating highly efficient thick OSCs.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,energy & fuels