Correlation of Fabrication Methods and Enhanced Wear Performance in Nanoporous Anodic Aluminum Oxide with Incorporated Molybdenum Disulfide (MoS2) Nanomaterials

Kendrich O’Donaghue Hatfield,Nathan Brown,Enkeleda Dervishi,Bradley Carpenter,Jordyn N. Janusz,Daniel E. Hooks
DOI: https://doi.org/10.3390/nano14050451
IF: 5.3
2024-02-29
Nanomaterials
Abstract:Wear performance is integral to component longevity, minimizing industrial waste and excess energy costs in a wide variety of applications. Anodized aluminum oxide (AAO) has many beneficial properties leading to its wide use across industries as a surface treatment for many aluminum components, but the wear properties of the coating could be improved significantly. Here, we used an electrochemical method to incorporate molybdenum disulfide (MoS2), a nanomaterial used as a dry lubricant, to modify alloys of aluminum during AAO preparation. Using Raman spectroscopy and tribological scratch measurements, we thoroughly characterized the structure and wear behavior of the films. The MoS2 deposition procedure was optimal on aluminum 5052 anodized in higher acid concentrations, with friction coefficients at around 0.05 (~10× better than unmodified AAO). Changing anodization conditions to produce harder films with smaller pores led to worsened wear properties, likely because of lower MoS2 content. Studying a commercial MoS2/AAO film of a different Al alloy (7075) showed that a heat treatment step intended to fully convert all deposited MoSx species to MoS2 can adversely affect wear in some alloys. While Al 6061 and 1100 produced films with worse wear performance compared to Al 5052 or 7075, our results show evidence that acid cleaning after initial anodization likely removes residual alloying elements, affecting MoS2 incorporation. This study demonstrates a nanomaterial modified AAO film with superior wear characteristics to unmodified AAO and relates fabrication procedure, film structure, and practical performance.
materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology,chemistry
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to improve the wear - resistant performance of nanoporous anodic aluminum oxide (AAO) coatings. Specifically, researchers incorporated molybdenum disulfide (MoS₂), a nanomaterial, as a dry lubricant into AAO by electrochemical methods to improve its wear - resistant characteristics. The paper explored the effects of different preparation parameters (such as acid concentration, heat treatment steps, aluminum alloy types, etc.) on the structure of MoS₂/AAO films and their actual wear - resistant performance. Through techniques such as Raman spectroscopy and tribological scratch measurement, researchers characterized the structure and wear behavior of the films in detail, aiming to reveal the relationship between the preparation method and the film performance, thereby providing guidance for industrial applications.