Effect of MoS2 and CeO2 Powder Addition by Friction Stir Processing on Wear and Corrosion Properties of Al7075 Alloy

Pabitra Maji,Ranit Karmakar,Rahul Kanti Nath,R. K. Bhogendro Meitei,Subrata Kumar Ghosh

DOI: https://doi.org/10.1007/978-981-16-0182-8_12

2021-01-01

Abstract:Aluminium alloys, a structural material owing to the great specific strength, are often subjected to extensive wear and corrosive environment. Considering the situation, in this article, a hybrid composite was made by integrating MoS2 and CeO2 powder in Al7075 alloy by friction stir processing. The SEM image of the microstructure of the composite reveals well dispersion of the powder particles in aluminium matrix. During sliding contact against WC ball, a significant decrease in friction coefficient of the composite is observed due to the presence of lubricating MoS2 powder. The SEM micrographs of the worn surfaces indicate that the oxidation and severe adhesive type of wear in aluminium are changed to a combination of abrasion and adhesion type of wear in the composite. The specific wear loss of around 8 × 10−4 mm3/N-m of the aluminium alloy is reduced to nearly 4 × 10−4 mm3/N-m by incorporating micro-reinforcements. In a solution of 3.5% NaCl, the corrosion current density is drastically reduced to 8.18 × 10−7 A/cm2 from 2 × 10−6 A/cm2 of unreinforced alloy. Also, the corrosion potential is increased from −863.962 to −672.192 mV due to the addition of hybrid reinforcement. Moreover, the rapid corrosion of aluminium alloy is reduced, and secondary passivation due to the presence of CeO2 is observed. Therefore, it is evident that the wear resistance and corrosion resistance of the Al7075 alloy are improved by the addition of MoS2 and CeO2 powder.